The invention provides a low cost and high strength foam concrete and a preparation method thereof. Low cost and high strength of foam concrete is provided, according to the quality of content, which comprises the following components of the prepared cement: 20 ~ 30%, 20 ~ 30% water gypsum, 10 ~ 15%, 10 ~ 20% of coal gangue, slag from 5 to 20%, the lightweight aggregate 0.5 ~ 30%, 0.5 ~ polymer emulsion 10%, fiber 0.2 ~ 5%, 0.5 ~ 25% foam, water reducing agent 0.05 ~ 2%. The experimental results show that the thermal conductivity of the low cost and high strength foam concrete provided by the invention is 0.05W/ (M = K), and the apparent dry density is 221kg/m
【技术实现步骤摘要】
一种低成本高强度泡沫混凝土及其制备方法
本专利技术涉及建筑材料
，特别涉及一种低成本高强度泡沫混凝土及其制备方法。
技术介绍
随着经济与社会的高速发展，能源问题日益成为我国经济发展的制约因素，能耗过大给资源与环境带来了不小的压力，而其中建筑能耗占我国总能耗的27％以上。外墙保温是降低建筑能耗的有效手段，而泡沫混凝土作为外墙保温材料，在建筑材料领域得到了广泛关注。泡沫混凝土是采用发泡剂制出泡沫，再将泡沫加入胶凝材料浆体，制成泡沫料浆，然后成型或现浇，经养护所形成的微孔轻质材料。泡沫混凝土由于密度小、吸水率低、保温隔热性能好等优势逐渐成为了研究重点。泡沫混凝土由胶凝材料、发泡剂和水等基本组分组成，在此基础上加入骨料、添加剂等。但现有的泡沫混凝土的成本较高，因此，需要使用低成本的原料来降低成本。矿渣是钢铁冶炼过程中排出的废渣，经过处理的矿渣具有较高的火山灰活性，在碱性环境下可以与水生成水硬性胶凝材料，将矿渣作为水泥的掺合料，不仅可以降低水泥成本，又改善了生态环境。中国专利CN102515664A公开了一种低成本超低密度泡沫混凝土，其主要成份为普通硅酸盐水泥、粉煤灰...
【技术保护点】
一种低成本高强度泡沫混凝土，按质量含量计，由包括以下组分的原料制备得到：水泥20～30％，石膏20～30％，水10～15％，煤矸石10～20％，矿渣5～20％，轻集料0.5～30％，聚合物乳液0.5～10％，纤维0.2～5％，泡沫0.5～25％，减水剂0.05～2％。
【技术特征摘要】
1.一种低成本高强度泡沫混凝土，按质量含量计，由包括以下组分的原料制备得到：水泥20～30％，石膏20～30％，水10～15％，煤矸石10～20％，矿渣5～20％，轻集料0.5～30％，聚合物乳液0.5～10％，纤维0.2～5％，泡沫0.5～25％，减水剂0.05～2％。2.根据权利要求1所述的低成本高强度泡沫混凝土，其特征在于，所述煤矸石的粒径为0.08～2mm。3.根据权利要求1或2所述的低成本高强度泡沫混凝土，其特征在于，所述煤矸石为未经煅烧的煤矸石。4.根据权利要求1所述的低成本高强度泡沫混凝土，其特征在于，所述矿渣的粒径为0.08～2mm。5.根据权利要求1所述的低成本高强度泡沫混凝土，其特征在于，所述轻集料包括有机轻集料和无机轻集料中的一种或多种。6.根据权利要求1所述的低成本高强度泡沫混凝土，其特征在于，所述聚合物乳液的质量浓度为40～8...
【专利技术属性】
技术研发人员：张新立，周莲，刘海静，李磊，
申请(专利权)人：中国建筑科学研究院，
类型：发明
国别省市：北京,11