烫金烫银型收缩套标标签及其制作方法技术
Bronzing and ironing type shrink sleeve label label and making method thereof
The invention relates to a manufacturing method of a bronzing type shrink sleeve label, which comprises the following steps: (a) providing printing material shrinkage material, the printing surface material with the outer main surface and the main surface; (b) in printed material in printing transparent non water soluble ink, and in blank printing water-based ink, obtained material I; (c) opposite wood I aluminizing treatment, get aluminum material; (d) the removal of aluminum material in non water soluble ink prepared, bronzing type sleeve label. The invention solves the market blank and the technical problem that the shrink sleeve label can not achieve the gilding effect, and provides the customer with a shrinkage label and a high-end design packing scheme.
【技术实现步骤摘要】
烫金烫银型收缩套标标签及其制作方法
本专利技术涉及收缩套标标签
，具体来说涉及真空镀铝和水洗实现一种烫金烫银金属效果的收缩套标标签制作方法。
技术介绍
收缩套标是一种印刷在塑料薄膜上的套筒式的标签，当对薄膜材料制成的这种标签进行加热时，标签会按照瓶体的曲线轮廓而收缩，使标签和瓶体完美结合在一起。收缩标签的主要应用领域是饮料业，此外，在个人护理品行业、食品和啤酒行业的增长势头也很大。收缩标签可以充分利用整个容器的表面，可以再现与传达对于图像及信息，大大增强包装产品的货架吸引力，同时收缩标签可以适应各种不同形状的容器，因而收缩膜套标在世界各地高速发展，2006年全球收缩标签平均增长率达到20％。收缩套标：将膜料先套在被帖物上，通过加温80度以上，自动收缩贴付在被贴物上，其名为收缩套标，适合各种被帖物。转印膜：使用方法是必须要加热120度以上、加压透过热转印机压烫在被贴物上，其名称为热转印膜，适合有锥度、平面无异性的被贴物。收缩膜与转印膜等其他膜不同，对于温度更为敏感，因此无法进行热烫和冷烫处理，对亮色金属效果的加工效果难度比其他膜相比技术难度更大。在传统的收缩套...
【技术保护点】
一种烫金烫银型收缩套标标签的制作方法,其特征在于,包括以下步骤:(a)提供收缩材质的印刷面材,所述印刷面材具有外主表面和里主表面；(b)在印刷面材里印透明非水溶性油墨,并且在空白处印刷水溶性油墨,得到面材I；(c)对面材I进行镀铝处理，得到镀铝面材；(d)去除镀铝面材中的非水溶性油墨，制得烫金烫银型套标标签。
【技术特征摘要】
1.一种烫金烫银型收缩套标标签的制作方法,其特征在于,包括以下步骤:(a)提供收缩材质的印刷面材,所述印刷面材具有外主表面和里主表面；(b)在印刷面材里印透明非水溶性油墨,并且在空白处印刷水溶性油墨,得到面材I；(c)对面材I进行镀铝处理，得到镀铝面材；(d)去除镀铝面材中的非水溶性油墨，制得烫金烫银型套标标签。2.根据权利要求1所述的制作方法，其特征在于，步骤(d)中还包括在去除非水溶性油墨后，在镀铝面涂布镀铝保护液。3.根据权利要求2所述的制作方法，其特征在于，通过涂布机在镀铝面涂布镀铝保护液。4.根据权利要求2所述的制作方法，其特征在于，还包括步骤(e)对烫金烫银型套标标签进行合掌成型。5.根据权利要求1所述的制作方法，其特征在于，步骤(b)中采用真空镀铝...
【专利技术属性】
技术研发人员：鞠进元，李浩，
申请(专利权)人：上海鸿元展印有限公司，
类型：发明
国别省市：上海,31