The invention relates to an antistatic pad, in particular to a durable antistatic pad and a preparation method thereof. A durable antistatic pad, the persistence of anti static radio pad is mainly made from the following raw materials by weight: 100 PVC, 20~80 two phthalic acid ester plasticizer, 1~15 composite antistatic agent, 10~40 parts of light calcium carbonate, 3~10 chlorinated paraffin, 1~7 stearate 3~8, a zinc organic acid based stabilizer, 1~3 phr, the composite antistatic agent for nano copper, polyether amide dispersant and ethylene bistearic amide (EBS) blends. The durable antistatic radio pad made by the invention has the advantages of long antistatic durability, stable product performance and wide application range, and is suitable for the manufacture of various electronic products.
【技术实现步骤摘要】
一种持久性抗静电台垫及其制备方法
本专利技术涉及一种抗静电台垫，特别涉及一种持久性抗静电台垫及其制备方法。
技术介绍
抗静电台垫作为特种的高分子材料，主要用于电子半导体器件、计算机、电子通讯设备和集成电路等微电子工业的生产车间、试验室，以及医院手术室、CT、X射线室、CCU、ICU病房的地坪、工作台面和内装饰。传统抗静电贴面板主要在三合板表层油漆中或橡胶板内添加小分子的抗静电剂，迁移到表面的抗静电剂与空气中水分子结合，形成导电通路并释放静电。这类产品中抗静电剂易挥发，产品寿命短，一般在6个月左右；另一方面，静电排放效果易受空气、湿度等环境因素影响，尤其在北方干燥环境中面板的表面电阻值高，随着时间推移抗静电指标衰减快，静电释放不稳定。目前制备抗静电高分子材料常用的方法是在聚合物基材中添加一定量的有机分子抗静电剂降低聚合物表面电阻和体积电阻，增加导电性，达到防止制品上电荷聚集的目的。然而由于有机分子抗静电剂与基体相容性差易于迁移，在高温加工和使用过程中容易从基体中析出导致材料抗静电性能不够持久。常规的无机抗静电剂如炭黑、金属粉末等，虽能有效提高抗静电材料的导电性能，但...
【技术保护点】
一种持久性抗静电台垫，其特征在于该持久性抗静电台垫主要是由如下以重量份计的原料制成：100份PVC、20~80份邻苯二甲酸酯增塑剂、1~15份复合抗静电剂、10~40份轻质碳酸钙、3~10份氯化石蜡、1~7份硬脂酸、3~8份锌系有机基稳定剂、1~3份防老剂，所述的复合抗静电剂为纳米铜、聚醚酰胺和分散剂乙撑双硬脂酰胺（EBS)的共混物。
【技术特征摘要】
1.一种持久性抗静电台垫，其特征在于该持久性抗静电台垫主要是由如下以重量份计的原料制成：100份PVC、20~80份邻苯二甲酸酯增塑剂、1~15份复合抗静电剂、10~40份轻质碳酸钙、3~10份氯化石蜡、1~7份硬脂酸、3~8份锌系有机基稳定剂、1~3份防老剂，所述的复合抗静电剂为纳米铜、聚醚酰胺和分散剂乙撑双硬脂酰胺（EBS)的共混物。2.根据权利要求1所述的持久性抗静电台垫，其特征在于：所述的复合抗静电剂中，聚醚酰胺、纳米铜和EBS的质量比为100:0.1~5：0.1~0.5。3.根据权利要求1所述的...
【专利技术属性】
技术研发人员：方国忠，陈志勇，
申请(专利权)人：台州博尔特塑胶电子有限公司，
类型：发明
国别省市：浙江,33