The utility model relates to a zero rotating steel wire rope of a heat thawing filling material. A heat melting wire rod is arranged between the rope strands of the steel wire rope, and the diameter of the heat melting wire monofilament is between 0.2~0.5mm, and the heat melting wire rod is added at least at least when the wire rope is twisted. The utility model relates to a wire rope of hot melt filling material, through heating in the subsequent processing, close integration with external material, give full play to the steel wire skeleton performance, while such wire rope in the follow-up process requires the use of lower residual stress, pulled out of the 20 meters test rotary < 2 rpm, and to avoid wire rope integration tape does not occur in the upper and lower axial deflection operation problems.
【技术实现步骤摘要】
热融性填充材料的零回转钢丝绳
本技术涉及一种热融性填充材料的零回转钢丝绳。
技术介绍
现有的钢丝绳内没有填充材料(参见图4),与外层覆盖材料结合力差,此种钢丝绳在后续使用过程中,残余应力高,同时与钢丝绳整合的带子在上下运行过程中会发生轴向偏转的问题。
技术实现思路
本技术的目的在于克服上述不足,提供了一种热融性填充材料的零回转钢丝绳,其在后续加工中通过加热,与外部材料紧密融合,充分发挥钢丝绳骨架性能,同时此类钢丝绳在后续使用过程中要求更低的残余应力,拉出20米测试回转<2转,才能避免与钢丝绳整合的带子在上下运行过程中不发生轴向偏转的问题。本技术的目的是这样实现的:一种热融性填充材料的零回转钢丝绳,其特点是:所述钢丝绳的绳股之间设置有热融性线材,热融性线材单丝直径0.2~0.5mm之间,在钢丝绳捻制过程中加入,所述热融性线材至少有一根,此钢丝绳在后续生产皮带时,预热至180度左右,钢丝绳内部聚氨酯线逐渐融化,在挤塑过程中绳股与外部聚氨酯料相结合。与现有技术相比,本技术的有益效果是:本技术一种热融性填充材料的零回转钢丝绳,在钢丝绳捻制生产过程中加入适量的热融性填充材料,使得钢丝绳在后续深加工中,可融材料与橡胶类、聚酯类覆盖层发生化学反应,有效的融为一体,提升钢丝绳与外覆盖材料的粘合力。同时这种钢丝绳的残余应力低,拉出20米测试回转<2转,在制作PU带或同步电缆随行带时保持带子的直线性、无扭转性。附图说明图1为本技术一种热融性填充材料的零回转钢丝绳的结构示意图。图2为热融性填充材料的零回转钢丝绳预热时的示意图。图3为钢丝绳与热融性填充材料相结合后的示意图。图4为普通 ...
【技术保护点】
一种热融性填充材料的零回转钢丝绳,其特征在于:所述钢丝绳的绳股(1)之间设置有热融性线材(2),热融性线材(2)单丝直径0.2~0.5mm之间,在钢丝绳捻制过程中加入,所述热融性线材(2)至少有一根,所述热融性线材(2)为聚氨酯线。
【技术特征摘要】
1.一种热融性填充材料的零回转钢丝绳,其特征在于:所述钢丝绳的绳股(1)之间设置有热融性线材(2),热融性线材(2)单...
【专利技术属性】
技术研发人员:唐健,董东,张伦,陈哲,夏晓东,陈硕彦,许晓楠,许铭锋,陈爱华,
申请(专利权)人:江苏法尔胜精细钢绳有限公司,
类型:新型
国别省市:江苏,32