The invention discloses a high-efficient anticorrosion coating with a high speed railway subgrade, which consists of the following components by weight: made of bisphenol A type epoxy resin 50 ~ 70, 5 ~ 15 polyaniline nano microspheres, potassium titanate whiskers from 0.5 to 5, 10 to 30 portions of diatomite, carboxymethyl cellulose 5 ~ 15 silica powder 0.1 ~ 2, 15 ~ 30, solvent. High performance anticorrosion coating of the invention in components, especially in bisphenol A epoxy resin, polyaniline nano microspheres and potassium titanate whisker, mutual synergy, can make the coating has high hardness and high, high adhesion, high mechanical strength, high impact resistance and high temperature performance, has a good application prospect.
【技术实现步骤摘要】
高铁客运专线路基用高效防腐涂料
本专利技术属于涂料
，具体地说涉及一种高铁客运专线路基用高效防腐涂料。
技术介绍
钢铁广泛的应用于工业生产和日常生活中，但是由于化学腐蚀、电化学腐蚀、生物腐蚀等造成的钢铁的损失量占到了全球每年钢铁产量的30%左右，而且被腐蚀的钢铁是无法收回再利用的，腐蚀造成了巨大的直接或间接经济损失和严重的社会危害。在资源日益匮乏的今天，通过采取恰当的腐蚀控制技术与手段，最大限度的减缓和控制金属腐蚀，不仅可以减少损失，还有利于资源的可持续利用。在已经发展起来的腐蚀防护技术中，涂料涂层防腐技术应用最为广泛，但如何获得高硬高、高附着力、高机械强度和耐高温的防腐涂料仍是需要解决的问题目。
技术实现思路
本专利技术的目的是在现有技术的基础上，提供一种高效防腐涂料。本专利技术的另一目的是提供一种上述高效防腐涂料的制备方法。本专利技术的目的可以通过以下措施达到：一种高铁客运专线路基用高效防腐涂料，它由如下重量份的组分制成：双酚A型环氧树脂50～70份，聚苯胺纳米微球5～15份，钛酸钾晶须0.5～5份，硅藻土10～30份，羟甲基纤维素5～15份，二氧化硅粉0....
【技术保护点】
一种高铁客运专线路基用高效防腐涂料，其特征在于它由如下重量份的组分制成：双酚A型环氧树脂50～70份，聚苯胺纳米微球5～15份，钛酸钾晶须0.5～5份，硅藻土10～30份，羟甲基纤维素5～15份，二氧化硅粉0.1～2份，溶剂15～30份。
【技术特征摘要】
1.一种高铁客运专线路基用高效防腐涂料，其特征在于它由如下重量份的组分制成：双酚A型环氧树脂50～70份，聚苯胺纳米微球5～15份，钛酸钾晶须0.5～5份，硅藻土10～30份，羟甲基纤维素5～15份，二氧化硅粉0.1～2份，溶剂15～30份。2.根据权利要求1所述的高效防腐涂料，其特征在于它由如下重量份的组分制成：双酚A型环氧树脂55～65份，聚苯胺纳米微球5～15份，钛酸钾晶须0.5～3份，硅藻土15～25份，羟甲基纤维素5～15份，二氧化硅粉0.1～1份，溶剂15～30份。3.根据权利要求2所述的高效防腐涂料，其特征在于它由如下重量份的组分制成：双酚A型环氧树脂56～63份，聚苯胺纳米微球6～13份，钛酸钾晶须1～3份，硅藻土16～22份，羟甲基纤维素6～13份，二氧化硅粉0.1～1份，溶剂17～28份。4.根据权利要求1、2或3所述的高效防腐涂料，其特征在于所述溶剂为乙醇和环己酮。5.根据权利要求1、2或3所...
【专利技术属性】
技术研发人员：王景泉，
申请(专利权)人：滁州金桥德克新材料有限公司，
类型：发明
国别省市：安徽,34