一种阻燃塑料制造技术

本发明专利技术公开了一种阻燃塑料，它是由下述重量份数的物质制成：塑料100份、填料15‑25份，氰尿酸三聚氰胺10‑20份，三氧化钼5‑10份、聚磷酸铵5‑10份、聚对苯二甲酸丁二醇酯10‑20份、复合阻燃剂15‑30份，纳米二氧化钛1‑2份、助剂5‑10份。本发明专利技术一种阻燃塑料，塑料成分配制合理，成本适中，加入无机阻燃剂，具有无毒、低烟、使用寿命长的特点，可有效提升常规低熔点塑料的阻燃能力，并确保塑料良好的强度和耐磨性，使得低熔点塑料的应用范围更加广范。

Flame retardant plastic

The invention discloses a flame retardant plastics, it is prepared from the number of material: plastic packing 15 100 copies, 25 copies, 10 melamine cyanurate 20 copies, 10 copies, 5 MoO3 ammonium polyphosphate 5 10 copies, 10 of polybutylene terephthalate 20, composite flame retardant agent 15 30 copies, 2 copies, 1 nanometer titanium dioxide agent 5 10. The invention relates to a flame retardant plastics, plastic components for the formulation of reasonable, moderate cost, adding inorganic flame retardant, non-toxic, low smoke, long service life, can effectively improve the conventional low melting plastic flame retardant ability, and ensure the strength and wear resistance of plastic good, making the application of low melting point plastic wide.

【技术实现步骤摘要】
一种阻燃塑料
本专利技术涉及阻燃塑料领域，具体来说涉及一种环保阻燃塑料。
技术介绍
塑料广泛用于防火、防霉、防水、隔音、吸音、缓冲等领域，聚乙烯、聚丙烯、ABS等广泛应用于节水灌溉、建筑、室内装潢、家具、电力、运输等行业。但是常规塑料多数具有易燃性，特别是低熔点塑料，如：聚乙烯、聚苯乙烯、聚氯乙烯等，这对其制品的应用安全带来了诸多隐患。
技术实现思路
针对上述不足，本专利技术提供一种阻燃塑料，具有无毒、低烟，具有良好的强度和耐磨性的环保型阻燃塑料。本专利技术采用的技术方案如下：一种阻燃塑料，由下述重量份数的物质制成：塑料100份、填料15-25份，氰尿酸三聚氰胺10-20份，三氧化钼5-10份、聚磷酸铵5-10份、聚对苯二甲酸丁二醇酯10-20份、复合阻燃剂15-30份，纳米二氧化钛1-2份、助剂5-10份。其中，所述复合阻燃剂为氢氧化铝、氢氧化镁、硼酸锌、氧化钙中的任意几种。本专利技术的有益效果：本专利技术采用无机阻燃剂，无机阻燃剂具有无毒、无害、无烟、无卤的优点，本专利技术采用的塑料成分配制合理，成本适中，可有效提升常规低熔点塑料的阻燃能力，并确保塑料良好的强度和耐磨性，使得低熔点塑本文档来自技高网...

【技术保护点】
一种阻燃塑料，其特征在于：它是由下述重量份数的物质制成：塑料100份、填料15‑25份，氰尿酸三聚氰胺10‑20份，三氧化钼5‑10份、聚磷酸铵5‑10份、聚对苯二甲酸丁二醇酯10‑20份、复合阻燃剂15‑30份，纳米二氧化钛1‑2份、助剂5‑10份。

【技术特征摘要】
1.一种阻燃塑料，其特征在于：它是由下述重量份数的物质制成：塑料100份、填料15-25份，氰尿酸三聚氰胺10-20份，三氧化钼5-10份、聚磷酸铵5-10份、聚对苯二甲酸丁二醇酯10...

【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：东至县科创塑料制品有限公司，
类型：发明
国别省市：安徽,34