一种方管冷拔用抗震无渗漏酸洗槽制造技术
Shock resistant non leakage pickling bath for square tube cold drawing
The present invention relates to a pickling bath with cold drawn tubes in miscellaneous tube drawing pickling, pickling tank of the tank from outside to inside comprises the structure layer, middle layer and seismic rigid layer, the structure layer is composed of cement casting steel cage, the cage extends downward to the trough below 0.5 ~ 1m, the middle of earthquake layer is a multilayer structure of epoxy vinyl ester resin and glass cloth are arranged at intervals, wherein the rigid wall and the bottom layer is arranged in the middle of the week in seismic layer surface. The pickling bath of the invention has the advantages of light weight, good corrosion resistance, good anti-seepage ability, long service life and low pressure resistance.
【技术实现步骤摘要】
一种方管冷拔用抗震无渗漏酸洗槽
本专利技术涉及一种对冷拔钢管酸洗的酸洗槽结构。
技术介绍
作为碳素钢、合金钢或不锈钢等机械结构用钢管的冷加工法，公知的有由拉拔机进行的拉拔加工法和由皮尔格式轧机进行的轧制加工法。其中，由拉拔机进行的拉拔加工法，与由皮尔格式扎机进行的轧制加工法相比，可以高效率地制造冷加工钢管。冷拔钢管的生产流程一般为热处理-酸洗-磷化-皂化-冷拔-退火，酸洗工序是利用硫酸对热处理后的钢材进行浸洗，现有酸洗槽结构容易发生渗漏，导致酸洗液向地面渗漏污染环境，且一旦发生渗漏、流失酸洗液的浓度也将变得不稳定而影响酸洗效果。
技术实现思路
本专利技术所要解决的技术问题是针对上述现有技术提供一种抗震无渗漏酸洗槽结构。本专利技术解决上述问题所采用的技术方案为：一种方管冷拔用抗震无渗漏酸洗槽，该酸洗槽的槽体由外向内依次包括结构层、中间抗震层和刚性层，所述结构层是由水泥浇注钢筋笼构成的，所述钢筋笼的支撑部分向下延伸至槽体以下0.5～1m，所述中间抗震层是环氧乙烯酯树脂和玻璃布间隔设置的多层结构，所述刚性层设置在中间抗震层的内周壁和底面。优选地，所述刚性层采用含75wt%二氧化硅的花岗岩拼成，具有良好的防腐性能。刚性层的厚度优选200±50mm。与现有技术相比，本专利技术的优点在于：提供了更加抗震防渗漏的酸洗槽，具有重量轻、耐腐蚀性能好、防渗能力好、使用寿命长、耐压无毒的优点。附图说明图1为本专利技术实施例中酸洗槽的结构示意图。具体实施方式以下结合附图实施例对本专利技术作进一步详细描述。如图1所示，本实施例中的方管冷拔用抗震无渗漏酸洗槽，该酸洗槽的槽体由外向内依次包...
【技术保护点】
一种方管冷拔用钢管冷拔酸洗液除杂用酸洗槽，其特征在于：酸洗槽的槽体由外向内依次包括结构层、中间抗震层和刚性层，所述结构层是由水泥浇注钢筋笼构成的，所述钢筋笼向下延伸至槽体以下0.5～1m，所述中间抗震层是环氧乙烯酯树脂和玻璃布间隔布置的多层结构，所述刚性层铺设在中间抗震层的内周壁和底面。
【技术特征摘要】
1.一种方管冷拔用钢管冷拔酸洗液除杂用酸洗槽，其特征在于：酸洗槽的槽体由外向内依次包括结构层、中间抗震层和刚性层，所述结构层是由水泥浇注钢筋笼构成的，所述钢筋笼向下延伸至槽体以下0.5～1m，所述中间抗震层是环氧乙烯酯树脂和玻璃布间隔布置的多层结构，所述刚性层铺设...