The invention relates to the field of new plastic materials, in particular to PPS composite material and method for a nano injection preparation, nano PPS composite material for injection molding, which comprises the following components in parts by weight of PPS resin, 50 80, continuous long carbon fiber 5 35 copies, 10 copies, 2 silica toughening agent 3 8 copies, 1 copies, 0.5 antioxidant coupling agent 0.5 2 copies, 1 copies of 0.5 lubricant; the toughening agent for maleic anhydride grafted styrene ethylene butadiene styrene; laser additive for copper nanoparticles modified by acrylate. The PPS composite material for nanometer injection molding of the invention has good mechanical performance, high binding force with metal material and good heat resistance, so as to better meet the requirements of NMT process.
【技术实现步骤摘要】
纳米注塑用PPS复合材料及其制备工艺
本专利技术涉及塑胶新材料领域，特别是涉及纳米注塑用PPS复合材料及其制备工艺。
技术介绍
纳米注塑成型，(NanoMoldingTechnology，NMT)是金属与塑胶以纳米技术结合的工艺方法。先将金属表面形成纳米微孔，塑胶直接射出成型在金属表面，让金属与塑胶可以一体成形，不但能够兼顾金属外观质感，也可以简化产品机构件设计，让产品更轻、薄、短、小，且较CNC工法更具成本效益；同时由于NMT是安全可回收的技术，对环境影响小。目前，可用于NMT成型的金属材料主要集中在铝材、镁材上，同时也有铜、不锈钢、钛、铁、紫铜多种金属进行粘结。可使用的树脂也有PBT、PPS、PA6、PA66等。NMT技术对树脂有以下要求：1、树脂要与一体注射成型的金属材料具有优异的结合力(180Kgf以上)；2、树脂材料的收缩率要尽可能低，一般要求低于0.3％，最好低于0.25％，以降低和金属材质之间的内应力；3、树脂材料耐热性高，有较好的耐金属降解能力，NMT成型过程的温度高达260℃～310℃，同时是和金属在同一个模具内同时成型的，要求树脂材料有较好的耐...
【技术保护点】
纳米注塑用PPS复合材料，其特征在于：包括以下重量份数的组分，PPS树脂50‑80份、连续长碳纤维5‑35份、二氧化硅2‑10份、增韧剂3‑8份、抗氧剂0.5‑1份、偶联剂0.5‑2份、润滑剂0.5‑1份；所述增韧剂为马来酸酐接枝苯乙烯‑乙烯‑丁二烯‑苯乙烯。
【技术特征摘要】
1.纳米注塑用PPS复合材料，其特征在于：包括以下重量份数的组分，PPS树脂50-80份、连续长碳纤维5-35份、二氧化硅2-10份、增韧剂3-8份、抗氧剂0.5-1份、偶联剂0.5-2份、润滑剂0.5-1份；所述增韧剂为马来酸酐接枝苯乙烯-乙烯-丁二烯-苯乙烯。2.根据权利要求1所述的纳米注塑用PPS复合材料，其特征在于：所述连续长碳纤维为沥青基碳纤维长丝；所述PPS树脂的重均分子量优选为40000～50000。3.根据权利要求2所述的纳米注塑用PPS复合材料，其特征在于：所述偶联剂为硅烷类偶联剂；所述抗氧剂为受阻酚类抗氧剂、亚磷酸酯类抗氧剂中的一种或多种；所述润滑剂由硅酮类和酰胺化合物组成。4.根据权利要求3所述的纳米注塑用PPS复合材料，其特征在于：包括以下重量份数的组分，PPS树脂58.5份、连续长碳纤维30份、二氧化硅5份、增韧剂3份、抗氧剂0.5份、偶联剂2份、润滑剂1...
【专利技术属性】
技术研发人员：贺鹏勇，贺朋波，
申请(专利权)人：深圳市华盈新材料有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。