The invention discloses a halogen-free flame retardant toughening polypropylene cable material and preparation method thereof, the basic formula and the weight ratio of 30: 40 group become polypropylene, maleic anhydride grafted 8 14 copies, 10 copies of 5 PPS, hyperbranched polymer 10 16 copies, 12 copies, 6 coupling agent halogen free flame retardant 15 22, 3 7 flame retardant synergist and coupling agent modified filler 12 18 copies, 5 copies of antioxidant 1. The preparation method of the invention is to send the material evenly mixed into the feeding hopper of the double screw extruder and extrude and granulate through the double screw extruder. The polypropylene cable material prepared by the invention has the advantages of high mechanical strength, good elasticity and flame retardance, excellent abrasion resistance and tear resistance, and is suitable for the field of wire and cable.
【技术实现步骤摘要】
一种无卤阻燃增韧聚丙烯电缆料及其制备方法
本专利技术涉及电线电缆料领域，尤其涉及一种无卤阻燃增韧聚丙烯电缆料及其制备方法。
技术介绍
聚丙烯（PP）是一种半结晶的热塑性塑料，具有较高的耐冲击性，机械性质强韧，抗多种有机溶剂和酸碱腐蚀，广泛应用于电线电缆、建筑材料、汽车工业、家用电器、包装材料等方面。由于聚丙烯阻燃性能差，极易燃烧，其极限氧指数（LOI）为18.5，遇火燃烧时发热量高、燃烧速度快、并伴有发烟、滴落等现象，限制了它在电线电缆领域的应用。现在市场上销售的大多属于经过添加无卤阻燃剂改性后的聚丙烯电缆料。然而，目前市场上的无卤阻燃聚丙烯电缆料普遍存在力学强度和弹性差、不耐磨，虽然具有阻燃功能，但是阻燃剂添加量的大、阻燃效果差，一定程度上限制了聚丙烯电缆料的应用。
技术实现思路
本专利技术目的在于克服现有技术中的缺陷，提供一种无卤阻燃增韧聚丙烯电缆料,其力学强度高、弹性和阻燃效果好、耐磨抗撕裂性能优异。同时，本专利技术还提供了一种无卤阻燃增韧聚丙烯电缆料的制备方法。为达到上述目的，本专利技术是通过以下技术方案实现的：一种无卤阻燃增韧聚丙烯电缆料，基本配方和重量比组...
【技术保护点】
一种无卤阻燃增韧聚丙烯电缆料，其特征在于，基本配方和重量比组成为：聚丙烯 30‑40份、马来酸酐接枝物8‑14份、聚苯硫醚 5‑10份、超支化聚合物10‑16份、偶联剂6‑12份、无卤阻燃剂15‑22份、阻燃增效剂 3‑7份、偶联剂改性填料12‑18份、抗氧剂1‑5份。
【技术特征摘要】
1.一种无卤阻燃增韧聚丙烯电缆料，其特征在于，基本配方和重量比组成为：聚丙烯30-40份、马来酸酐接枝物8-14份、聚苯硫醚5-10份、超支化聚合物10-16份、偶联剂6-12份、无卤阻燃剂15-22份、阻燃增效剂3-7份、偶联剂改性填料12-18份、抗氧剂1-5份。2.根据权利要求1所述的无卤阻燃增韧聚丙烯电缆料，其特征在于：所述聚丙烯为无规共聚聚丙烯。3.根据权利要求1所述的无卤阻燃增韧聚丙烯电缆料，其特征在于：所述马来酸酐接枝物为马来酸酐接枝聚丙烯。4.根据权利要求1所述的无卤阻燃增韧聚丙烯电缆料，其特征在于：所述聚苯硫醚为粉状聚苯硫醚。5.根据权利要求1所述的无卤阻燃增韧聚丙烯电缆料，其特征在于：所述超支化聚合物为端羟基超支化聚酯、端羟基超支化聚酰胺酯中的至...
【专利技术属性】
技术研发人员：刘凤姐，
申请(专利权)人：泉州盈创新材料技术开发有限公司，
类型：发明
国别省市：福建,35