The invention discloses a water immersion wooden high gloss varnish and a preparation method thereof, which relates to the technical field of coatings. According to the weight percentage is composed of the following components: waterborne crosslinking acrylic emulsion 35 45%, Waterborne Aliphatic Polyurethane Dispersion 35 45% 10 15%, deionized water, defoaming agent 0.1 0.5% propylene glycol butyl ether 1 3%, 2 4% anti settling agent, substrate wetting agent 0.1 0.5% 0.1, thickener 0.5%; waterborne crosslinking acrylic emulsion MFFT to 31 DEG C. The water-based wood high gloss varnish has the advantages of low VOC content and good anti flow performance, and is suitable for dipping and coating construction, and has wide application prospect.
【技术实现步骤摘要】
一种浸涂用水性木器高光清漆及其制备方法
本专利技术涉及涂料
技术介绍
化妆刷、画笔的木柄一般选用桦木制成，其木质坚硬、不易变形，表面采用涂料使其具有丰富的色彩，以起到装饰和保护的效果。由于木柄的形状多样，喷涂难以实现，一般采用浸涂的方式施工。目前生产厂家一般使用快干的溶剂型涂料，其中主要是硝基漆。硝基漆依靠添加大量的快干有机溶剂来实现其快干性，在使用过程中还要采用有机溶剂稀释，有机溶剂含量可高达50%及以上。在环境湿度超过60%时，需要降低环境湿度以防止漆膜发白的弊病。浸涂槽在施工过程中需要敞口放置，工人在操作过程中会吸入大量的有机溶剂，长时间操作对身体产生极大的危害，并且溶剂型涂料易燃易爆，时刻存在安全隐患。《HJ2537-2014环境标志产品技术要求水性涂料》中水性木器涂料对VOC（挥发性有机化合物）的限制为80g/L。水性涂料以其低VOC的环保特性，比溶剂型涂料更适合浸涂施工。中国专利CN102051096A中采用的高Tg自交联丙烯酸乳液，需要加很多溶剂才能室温成膜，溶剂用量达配方总量的4-16%，制得的产品VOC高达235g/L，已不能满足现有标...
【技术保护点】
一种浸涂用水性木器高光清漆，其特征在于：按重量百分比由以下组分组成：水性自交联丙烯酸乳液35‑45%，水性脂肪族聚氨酯分散体35‑45%，去离子水10‑15%，消泡剂0.1‑0.5%，丙二醇丁醚1‑3%，防沉剂2‑4%，底材润湿剂0.1‑0.5%，增稠剂0.1‑0.5%；所述水性自交联丙烯酸乳液的MFFT为31℃。
【技术特征摘要】
1.一种浸涂用水性木器高光清漆，其特征在于：按重量百分比由以下组分组成：水性自交联丙烯酸乳液35-45%，水性脂肪族聚氨酯分散体35-45%，去离子水10-15%，消泡剂0.1-0.5%，丙二醇丁醚1-3%，防沉剂2-4%，底材润湿剂0.1-0.5%，增稠剂0.1-0.5%；所述水性自交联丙烯酸乳液的MFFT为31℃。2.根据权利要求1所述的一种浸涂用水性木器高光清漆，其特征在于所述水性自交联丙烯酸乳液为荷兰帝斯曼DSM公司的NeoCrylXK-12。3.根据权利要求1所述的一种浸涂用水性木器高光清漆，其特征在于所述水性脂肪族聚氨酯分散体为荷兰帝斯曼DSM公司的NeoRezR-2180。4.根据权利要求1所述的一种浸涂用水性木器高光清漆，其特征在于所述防沉剂为聚酰胺钠铵盐。5.根据权利要求4所述的一种浸涂用水性木器高光清漆，其特征在于所述防沉剂为日本帝斯巴隆DISPARLO...
【专利技术属性】
技术研发人员：王瑞宏，郭晓峰，郭晓猛，