The invention discloses an unsaturated polyester resin strap crafts manufacturing method, the invention is achieved by the following technical scheme: (1) unsaturated polyester resin from certain quality, in accordance with the addition of accelerator and curing agent, the proportion of mixing in a vacuum oven vacuum stirring 5~10min removal of bubbles; (2) the chain end into the mold, but also in the mold into the dried plant, plastic products such as decorative arts and crafts; (3) to mold into chouwan vacuum resin, resin curing at 0 DEG ~80 DEG in the oven, the mold is opened out the crude polished finished, the the invention can be used for making bracelets, anklets, necklaces and other ornaments crafts, time-saving, reduces the production cost.
【技术实现步骤摘要】
一种不饱和聚酯树脂挂饰工艺品制作方法
本专利技术涉及树脂工艺品制作领域，具体为一种不饱和聚酯树脂挂饰工艺品制作方法。
技术介绍
近年来，随着国家经济的迅速发展，人们的生活水平的快速提高，树脂工艺品越来越受使用者的青睐。目前市场上的树脂工艺品挂饰，挂链和树脂饰品基本都是分离开的，佩戴过程中容易脱落，而且制作费时费力，无意中提高了成本；本专利技术提供一种不饱和聚酯树脂挂饰工艺品制作方法，可以用于制作手链、脚链、项链等挂饰工艺品，省时省力，降低了制作成本。
技术实现思路
本专利技术提供一种不饱和聚酯树脂挂饰工艺品制作方法，旨在降低树脂挂饰工艺品的制作成本和制作时间，本专利技术通过下述技术方案来实现：一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，本工艺品树脂部分由以下原料组成：一定量的不饱和聚酯树脂，以及占树脂质量0~4%的促进剂和树脂质量1~3%的固化剂。一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，制作挂饰的挂链可以是金属挂链、织物编织挂链或者塑料挂链。一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，也可在模具中放入干燥后的植物、塑料制品等作为工艺品的装饰物；所述的不饱和聚酯树脂的型号可以是196S；所述的促进剂可以是对苯二胺，固化剂可以是过氧化苯甲酰；本专利技术不饱和聚酯树脂挂饰工艺品的制作方法：（1）取一定质量的不饱和聚酯树脂，按照上述比例加入促进剂和固化剂，搅拌均匀，放入真空烘箱中抽真空5~10min去除搅拌产生的气泡；（2）将挂链一端放入模具中，也可在模具中放入干燥后的植物、塑料制品等作为工艺品的装饰物；（3）向模具中倒入抽完真空的树脂，在0℃~...
【技术保护点】
一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，本工艺品树脂部分由以下原料组成：一定量的不饱和聚酯树脂，以及占树脂质量0~4%的促进剂和树脂质量1~3%的固化剂。
【技术特征摘要】
1.一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，本工艺品树脂部分由以下原料组成：一定量的不饱和聚酯树脂，以及占树脂质量0~4%的促进剂和树脂质量1~3%的固化剂。2.根据权利要求1所述的一种不饱和聚酯树脂挂饰工艺品制作方法如下所示，（1）取一定质量的不饱和聚酯树脂，按照一定...
【专利技术属性】
技术研发人员：王春红，陈祯，刘胜凯，李锡伯，张桂燕，
申请(专利权)人：天津金衫易德塑料包装有限责任公司，
类型：发明
国别省市：天津,12