The invention discloses a preparation method of pressing solid tyre with tread rubber and preparation, wherein the tread rubber comprises the following components: natural rubber, styrene butadiene rubber, graphene, stearic acid, aromatic oil, carbon black, curing agent, accelerating agent, reinforcing agent, bulking agent, antioxidant. The preparation method comprises: firstly, natural rubber, styrene butadiene rubber added into a reaction kettle, heating to melt, then adding graphene modified; the mixture is added to the mixer, then add the remaining ingredients, mixing and discharging, to obtain the tread. The tread rubber used in the solid tyre not only makes the tire better wear resistance and tear resistance, but also has certain flame retardancy and corrosion resistance, and greatly prolongs the service life of the solid tyre.
【技术实现步骤摘要】
一种压配式实心轮胎用胎面胶及制备方法
本专利技术涉及实心轮胎
，具体涉及一种压配式实心轮胎用胎面胶及制备方法。
技术介绍
实心橡胶轮胎是一种用于高负荷、苛刻使用条件下运行的工业车辆轮胎，广泛用于各种工业车辆、军事车辆、建筑机械及空中列车等。但是，在车辆行驶过程中，实心橡胶轮胎温升明显，存在高温爆裂、崩花掉块等现象，尤其在越野及矿用路面，实心轮胎胎面胶存在抗切割能力差问题。实心轮胎胎面胶材料必须具有高模量、低生热、高导热、高疲劳、高强度、抗撕裂等综合优异性能，方能满足使用需求。随着工业车辆和其它特殊用途车辆的发展，对轮胎性能的要求越来越高。实心轮胎因具有较高的负荷能力、行驶平稳、耐扎刺、无需经常修补等特点而被广泛应用于工程车辆等低速车辆上。受到广大消费者的青睐，为实心轮胎市场带来无限商机。我国汽车工业、采矿业、采煤业、金属冶炼行业的迅猛发展和消防、隔离易燃物品等方面的需要，对橡胶产品的阻燃导电性能提出了更高要求，对其需求量呈现出快速增长态势。但目前大多数的合成橡胶都是可燃或易燃胶种，耐磨性不好，由此带来了潜在的火灾危害性，给生产生活带来了诸多不便。因此，研究开...
【技术保护点】
一种压配式实心轮胎用胎面胶，其特征在于：包括如下重量份的各原料：天然橡胶20~36份、丁苯橡胶12~25份、石墨烯1.5~4.5份、硬脂酸10~15份、芳烃油8~17份、炭黑15~22份、硫化剂3~10份、促进剂6~11份、增强剂8~16份、填充剂12~18份、防老剂3~8份。
【技术特征摘要】
1.一种压配式实心轮胎用胎面胶，其特征在于：包括如下重量份的各原料：天然橡胶20~36份、丁苯橡胶12~25份、石墨烯1.5~4.5份、硬脂酸10~15份、芳烃油8~17份、炭黑15~22份、硫化剂3~10份、促进剂6~11份、增强剂8~16份、填充剂12~18份、防老剂3~8份。2.根据权利要求1所述的压配式实心轮胎用胎面胶，其特征在于：所述天然橡胶32份、丁苯橡胶20份、石墨烯3份、硬脂酸12份、芳烃油15份、炭黑18份、硫化剂7份、促进剂9份、增强剂12份、填充剂16份、防老剂5份。3.根据权利要求1所述的压配式实心轮胎用胎面胶，其特征在于：所述硫化剂为硫磺和硫化剂DTDM，其中两者的质量比为1:0.8~2。4.根据权利要求1所述的压配式实心轮胎用胎面胶，其特征在于：所述促进剂为促进剂NOBS、促进剂TBBS中的任一种。5.根据...
【专利技术属性】
技术研发人员：卞泽根，
申请(专利权)人：明光速耐德实心轮胎有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。