The present invention relates to a spray welding with cobalt chromium tungsten alloy powder and method of use thereof, which comprises the following components: the mass percentage of C was 3 ~ 4%, Cr is 35 ~ 45%, Si is 0.5 ~ 0.9%, W is 15 ~ 17%, Fe is 0.1 ~ 0.5%, Mn is 1 ~ 2%, 1 ~ 2% Mo Ni, from 4 to 5%, the rest is Co. The method comprises the steps as follows: the first step: surface treatment; the second step: cobalt chromium tungsten alloy powder; drying process; the third step: fourth step: by plasma powder welding equipment to cobalt chromium tungsten alloy powder surfacing in the workpiece surface. The present invention has excellent properties of heat resistance, corrosion resistance, high red hardness and so on. The impact strength is bad, and the tendency of cracking is sensitive in the process of surfacing. After surfacing the surface of the workpiece to be worn, the repair of the worn part can be realized, and the recovery and reuse of the worn workpiece can be realized. The invention can also weld the surface of the new workpiece, thus achieving the function of pre protection.
【技术实现步骤摘要】
喷焊用钴铬钨合金粉及其使用方法
本专利技术涉及焊接加工
，具体地说是喷焊用钴铬钨合金粉及其使用方法。
技术介绍
螺旋推进器，装在轮船尾部的加速装置。在使用一段时间后，螺旋推进器会出现磨损，影响到轮船的正常加速行驶，也会导致螺旋推进器的使用寿命急剧缩短。若进行更换新的螺旋推进器，成本较高。又如泵叶阀座、轴承，当使用时产生一定程度的磨损时，需要及时的进行更换，否则会影响到正常的安装定位和运动传递，然而更换又会导致设备使用的成本增加。以上三种部件，若采用更换，磨损后的部件会被丢弃，导致沿着的资源浪费，迫切需要一种可将上述磨损的部件进行尺寸修复，从而实现回收再利用的材料。
技术实现思路
为了解决现有技术中的不足，本专利技术提出喷焊用钴铬钨合金粉及其使用方法。本专利技术所要解决的技术问题采用以下技术方案来实现：喷焊用钴铬钨合金粉，包括以下质量百分比的组分：C为3～4％、Cr为35～45％、Si为0.5～0.9％、W为15～17％、Fe为0.1～0.5％、Mn为1～2％、Mo为1～2％、Ni为4～5％、余量为Co。喷焊用钴铬钨合金粉的使用方法，所述方法步骤如下：第一步：工件...
【技术保护点】
喷焊用钴铬钨合金粉，其特征在于：包括以下质量百分比的组分：C为3～4％、Cr为35～45％、Si为0.5～0.9％、W为15～17％、Fe为0.1～0.5％、Mn为1～2％、Mo为1～2％、Ni为4～5％、余量为Co。
【技术特征摘要】
1.喷焊用钴铬钨合金粉，其特征在于：包括以下质量百分比的组分：C为3～4％、Cr为35～45％、Si为0.5～0.9％、W为15～17％、Fe为0.1～0.5％、Mn为1～2％、Mo为1～2％、Ni为4～5％、余量为Co。2.喷焊用钴铬钨合金粉的使用...
【专利技术属性】
技术研发人员：程敬卿，薛卫昌，周乾坤，
申请(专利权)人：安徽再制造工程设计中心有限公司，
类型：发明
国别省市：安徽,34