The invention provides a preparation method of modified nylon filament, which comprises the following steps: 1) the nylon filament winding on a self-made device, ultrasonic cleaning with acetone into the beaker after drying, then nylon fiber were placed in the room temperature treatment 20min CaCl2 methanol solution removed after drying; 2) extract preparation of antistatic additives or tank containing flame retardant additives; 3) immersion bath containing nylon filament into antistatic additives or flame retardant additives; 2) drawn from the extracts of nylon filament groove, through drying area, so as to obtain antistatic modified nylon filament or flame retardant nylon filament drying. The preparation method of the modified nylon filament can prepare an antistatic nylon filament or flame retardant modified nylon filament.
【技术实现步骤摘要】
一种改性锦纶长丝的制备方法
本专利技术涉及一种改性锦纶长丝的制备方法，属于化学纤维
技术介绍
锦纶，学名聚酰氨纤维，是中国所产聚酰胺类纤维的统称。国际上称尼龙。强度高.耐磨性,回弹性好，可以纯纺和混纺作各种衣料及针织品。主要品种有锦纶6和锦纶66，其物理性能相差不多。锦纶吸湿性和染色性都比涤纶好,耐碱而不耐酸，长期暴露在日光下其纤维强度会下降。锦纶有热定型特性,能保持住加热时形成的弯曲变形。锦纶的长丝可制成弹力丝，短丝可与棉及晴纶混纺，以提高其强度和弹性.除了在衣着和装饰品方面的应用外，还广泛应用在工业方面如帘子线，传动带，软管，绳索，渔网等。锦纶的品种很多，有锦纶6、锦纶66、锦纶11、锦纶610其中最主要的是锦纶66和锦纶6。广泛应用在工业方面如帘子线，传动带，软管，绳索，渔网等。纳米尼龙的优点在于其热性能、力学性能、阻燃性、阻隔性比纯尼龙高，而制造成本与普通尼龙相当。为了提高和改善锦纶的物化性能，增加服用功能，人们对锦纶纤维进行了改性，目前的改性锦纶纤维种类还不够丰富。
技术实现思路
本专利技术的目的是克服现有设计的不足，提供一种改性锦纶长丝的制备方法。本专利技术的改性锦纶长丝的制备方法，包括如下步骤：1）将锦纶长丝缠绕在自制的装置上，放入装有丙酮的烧杯中超声清洗后，烘干，再将锦纶纤维分别放入CaCl2-甲醇溶液中常温处理20min后取出干燥；2）准备含有抗静电添加剂或阻燃添加剂的浸液槽；3）锦纶长丝进入含有抗静电添加剂或阻燃添加剂的浸液槽；2）锦纶长丝从浸液槽引出后，再通过烘干区，从而得到干燥的抗静改性锦纶长丝或阻燃改性锦纶长丝。优选地，所述...
【技术保护点】
一种改性锦纶长丝的制备方法，其特征在于，包括如下步骤：1）将锦纶长丝缠绕在自制的装置上， 放入装有丙酮的烧杯中超声清洗后， 烘干， 再将锦纶纤维分别放入CaCl2‑甲醇溶液中常温处理20min后取出干燥；2）准备含有抗静电添加剂或阻燃添加剂的浸液槽；3）锦纶长丝进入含有抗静电添加剂或阻燃添加剂的浸液槽；2）锦纶长丝从浸液槽引出后，再通过烘干区，从而得到干燥的抗静改性锦纶长丝或阻燃改性锦纶长丝。
【技术特征摘要】
1.一种改性锦纶长丝的制备方法，其特征在于，包括如下步骤：1）将锦纶长丝缠绕在自制的装置上，放入装有丙酮的烧杯中超声清洗后，烘干，再将锦纶纤维分别放入CaCl2-甲醇溶液中常温处理20min后取出干燥；2）准备含有抗静电添加剂或阻燃添加剂的浸液槽；3）锦纶长丝进入含有抗静电添加...
【专利技术属性】
技术研发人员：陈礼荣，
申请(专利权)人：海安县华荣化纤有限公司，
类型：发明
国别省市：江苏,32