The invention belongs to the field of chemical coating, in particular to an anti fogging coating. Is composed of the following parts by weight: acrylate monomer 30-50, butyl acetate 30-45, modified surfactants 5-8, initiator 0.5-1.2, catalyst 0.01-0.05, active diluent 5-8, nonionic surfactant 15-20, modified fluorocarbon leveling agent 0.5-0.8, isopropanol 35-40 a copy of 40-55, deionized water. Antifogging coating provided by the invention, the formation of large hydrophilic acrylic resin, hydrophilic enough, can improve the water vapor in the film surface contact angle, so that the water vapor condenses into drops of water will not improve, anti fog effect, but also has simple preparation process, low equipment investment, low cost of raw materials, green environmental protection. The advantages of low VOC, low odor, and keep the clarity and smoothness of the surface of the substrate.
【技术实现步骤摘要】
一种防雾涂料
本专利技术属于化工涂料领域，具体是一种防雾涂料。
技术介绍
玻璃和透明塑料是人们日常生活中不可缺少的材料，使用这些材料，常常会遇到表面雾化问题，给人们的工作和生活带来了不便。所谓雾化，又称结雾，更确切称为结露，是指在高湿度下玻璃或透明塑料表面凝结成微小露珠的现象。表面起雾对生活带来的诸多不便，而且汽车普及性越来越高，人们对防雾也越来越重视。防雾的方法大致分为加热法和表面涂层法。加热法的原理是消除水蒸气与物体表面的温差，并加速水蒸气的干燥而达到防雾效果。这不仅会消耗更多的能源，而且操作比较困难。因为在北方或冬季，短时间内减少温差的操作难度比较大，尤其是大体积空间或冷车的情况下，防雾涂料有疏水型和亲水型两种，对亲水型防雾涂料研究较多，其防雾原理是利用高分子聚合涂层形成高亲水表面，使其对水的接触角变小，从而在表面形成极薄的水膜，进而起到防雾作用。目前用于防雾的涂料性能上参差不齐，质量不稳定或者效果不明显。
技术实现思路
为了解决上述问题，本专利技术提供了一种高性能防雾、持久、易操作的防雾涂料。本专利技术的技术方案如下：一种防雾涂料，是由以下重量份数的物质组成:丙烯酸酯单体30-50份、醋酸丁酯30-45份、改性的表面活性剂5-8份、引发剂0.5-1.2份、催化剂0.01-0.05份、活性稀释剂5-8份、非离子表面活化剂15-20份、改性氟碳流平剂0.5-0.8份、异丙醇35-40份、去离子水40-55份。进一步的，一种防雾涂料，改性的表面活化剂为含羧酸基团的表面活化剂，引发剂为偶氮二异丁腈，催化剂为单丁基氧化锡，活性稀释剂为季戊四醇三丙烯酸酯、二季戊四...
【技术保护点】
一种防雾涂料，其特征在于，是由以下重量份数的物质组成:丙烯酸酯单体30‑50份、醋酸丁酯30‑45份、改性的表面活性剂5‑8份、引发剂0.5‑1.2份、催化剂0.01‑0.05份、活性稀释剂5‑8份、非离子表面活化剂15‑20份、改性氟碳流平剂0.5‑0.8份、异丙醇35‑40份、去离子水40‑55份。
【技术特征摘要】
1.一种防雾涂料，其特征在于，是由以下重量份数的物质组成:丙烯酸酯单体30-50份、醋酸丁酯30-45份、改性的表面活性剂5-8份、引发剂0.5-1.2份、催化剂0.01-0.05份、活性稀释剂5-8份、非离子表面活化剂15-20份、改性氟碳流平剂0.5-0.8份、异丙醇35-40份、去离子水40-55份。2.如权利要求1所述...