一种人造石英石花纹板及其制备方法技术

本发明专利技术涉及人造石英石板技术领域，具体涉及一种人造石英石花纹板及其制备方法，其特征在于，包括按重量份数计的如下各组分：不饱和树脂8～10份，石英砂50～55份，混合色浆1～3份，石英粉30～35份，助剂1～2份；其中，所述石英砂经过4～6目的筛网过筛，所述石英粉经过600目的筛网过筛，所述助剂包括固化剂和促进剂。本发明专利技术的人造石英石花纹板具有环保、色泽鲜明透亮、易清洁、阻燃等优点。

A quartz stone plate and preparation method thereof

The present invention relates to artificial quartz stone technology field, in particular relates to a quartz stone plate and preparation method thereof, which is characterized by weight, including the following components: unsaturated resin 8 ~ 10, 50 ~ 55 quartz sand, mixed paste 1 ~ 3, 30 ~ quartz powder 35, agent 1 - 2; among them, the quartz sand after 4 ~ 6 mesh sieve, the quartz powder through 600 mesh sieve, the additives including curing agent and accelerant. The artificial quartz stone plate of the invention has the advantages of environmental protection, bright and bright color, easy cleaning and flame retardant, etc..

【技术实现步骤摘要】
一种人造石英石花纹板及其制备方法
本专利技术涉及建筑材料
，具体涉及一种人造石英石花纹板及其制备方法。
技术介绍
现有技术的人造石英石花纹板通常是通过不饱和树脂为粘接剂，与石英砂、颜料等进行搅拌后烘烤而直接制成人造石英石花纹板。现有技术制得的石英石花纹板通常颜色不鲜明透亮，花纹的颜色通常体现为石英砂和颜料本身的颜色，这样的石英石花纹板的花纹的颜色呆板不和谐。
技术实现思路
为了解决上述问题，本专利技术提供一种人造石英石花纹板及其制备方法，以不饱和树脂为粘合材料，与石英砂、混合色浆、助剂等充分搅拌均匀后，再经过烘烤、刮平、抛光等工序制得所述人造石英石花纹板，以解决现有人造石英石花纹板的透明度不好，花纹单调不和谐的技术缺陷。本专利技术提供的一种人造石英石花纹板，包括按重量份数计的如下各组分：不饱和树脂8～10份，石英砂50～55份，混合色浆1～3份，石英粉30～35份，助剂1～2份；其中，所述石英砂经过4～6目的筛网过筛，所述石英粉经过600目的筛网过筛，所述助剂包括固化剂和促进剂。优选地，所述混合色浆包括红、黄、棕、黑颜料。优选地，固化剂为乙烯基三胺。优选地，所述促进剂为间苯二酚。制本文档来自技高网...

【技术保护点】
一种人造石英石花纹板，其特征在于，包括按重量份数计的如下各组分：不饱和树脂8～10份，石英砂50～55份，混合色浆1～3份，石英粉30～35份，助剂1～2份；其中，所述石英砂经过4～6目的筛网过筛，所述石英粉经过600目的筛网过筛，所述助剂包括固化剂和促进剂。

【技术特征摘要】
1.一种人造石英石花纹板，其特征在于，包括按重量份数计的如下各组分：不饱和树脂8～10份，石英砂50～55份，混合色浆1～3份，石英粉30～35份，助剂1～2份；其中，所述石英砂经过4～6目的筛网过筛，所述石英粉经过600目的筛网过筛，所述助剂包括固化剂和促进剂。2.根据权利要求1所述的人造石英石花纹板，其特征在于：所述混合色浆包括红、黄、棕、黑颜料中的一种或数种组合。3.根据权利要求1所述的人造石英石花纹板，其特征在于：固化剂为乙烯基三胺。4.根据权利要求1所述的人造石英石花纹板，其特征...

【专利技术属性】
技术研发人员：胡北清，熊伟，
申请(专利权)人：广东必图新材料科技股份有限公司，
类型：发明
国别省市：广东,44