The invention belongs to the technical field of paper making, in particular to a high permeable paper and a preparation method thereof. The high permeable paper is made from the raw material of the following percentage of weight: wood pulp 90 to 97%; assistants 3 to 10%; wherein, the wood pulp is measured by an absolute dry quantity. The paper not only has high permeability and good permeability, high permeability, high uniformity, high resin content and good flexibility characteristics, and the downstream customers dipping, the wear resistant material is sprayed on the paper, then through high heat pressing, can be made of wood floors, with a high gloss, abrasion resistance and stability and the definition of wear-resistant paper can not achieve the common simulation results, the market prospect is very broad; the preparation method is simple, scientific and reasonable.
【技术实现步骤摘要】
高渗透纸及其制备方法
本专利技术属于造纸
，具体涉及一种高渗透纸及其制备方法。
技术介绍
目前，表层耐磨纸有3种生产工艺，第1种是在原纸生产过程中，在纸浆内添加耐磨料，所生产的耐磨纸，耐磨料没有包覆在纤维里面，大部分在纤维外部，在木地板热压过程中，耐磨料与模板紧密接触，对模板造成很大程度的磨损。通常情况下，使用带有耐磨剂的普通耐磨纸压贴地板时，一块模板在压贴4000压后，就必须重新更换模板，才能继续使用，否则地板表面光泽度会明显降低，严重影响强化木地板的亮度，及清晰度，所生产的强化木地板达不到客户使用要求。第2种是耐磨剂在原纸生产过程中涂在原纸上，由于纸机车速快，耐磨料分散不均匀，导致木地板的耐磨转数不稳定，制约着人们的正常使用。第3种是下游客户使用耐磨混合物(三聚氰胺胶+三氧化二铝等)喷涂在表层纸(原纸不含耐磨料)的上面。在压贴喷涂表层耐磨纸时，把喷涂耐磨混合料的一面放入背面压贴，模板的热压次数高达20000压以上才进行修复，是第一种生产工艺压贴次数的五倍。但是，由于原纸渗透差、柔软性差，上胶量低导致下游客户在浸渍喷涂时，耐磨混合物分散不均匀，严重影响强化...
【技术保护点】
一种高渗透纸，其特征在于：由如下重量百分数的原料制成：木浆 90～97％助剂 3～10％其中，木浆以绝干量计。
【技术特征摘要】
1.一种高渗透纸，其特征在于：由如下重量百分数的原料制成：木浆90～97％助剂3～10％其中，木浆以绝干量计。2.根据权利要求1所述的高渗透纸，其特征在于：由如下重量百分数的原料制成：木浆90～95％助剂5～10％。3.根据权利要求1所述的高渗透纸，其特征在于：所述的助剂由如下重量百分数的原料制成：硫酸铝0.2～3％聚丙烯酰胺0.5～4.5％湿强剂92.5～99.3％。4.根据权利要求1所述的高渗透纸，其特征在于：所述的木浆为漂白硫酸盐长纤维针叶木浆。5.一种权利要求1-4任一所述的高渗透纸的制备方法，其特征在于：步骤如下：(1)碎浆：首先将木浆加入到水力碎浆机内进行碎解；(2)磨浆：将步骤(1)所得碎浆后物质经过纤维疏解机将纤维疏解后，通过双盘磨打浆机打浆，将纤维切断、分丝帚化，得叩后木浆；(3)将步骤(2)所得叩后木浆泵入加填池内，然后将助剂加入加填池中搅拌混合，最后用水调节成浓度为2.5～3.0...
【专利技术属性】
技术研发人员：李安东，李文海，李洪利，丁福瑞，李学武，
申请(专利权)人：淄博欧木特种纸业有限公司，
类型：发明
国别省市：山东,37