负极锌膏及耐深度放电碱性电池制造技术
Negative zinc paste and alkali cell with deep resistance discharge
The invention discloses a negative electrode zinc paste, which does not produce dendritic material when the medium and small current intermittently discharges intermittently for a long time, and can not cause the internal short-circuit of the battery. A zinc electrode, zinc electrode is composed of the following components by weight: zinc alloy powder 66.20, polyacrylic acid 0.23, sodium polyacrylate, 0.46 KOH electrolyte 33.11; wherein, zinc alloy powder by bismuth, indium, lead and zinc, 195 g per gram of zinc containing bismuth alloy powder, 225 g per gram of indium containing zinc alloy powder, 225 g per gram of indium containing zinc alloy powder, lead per gram of zinc alloy powder for 6 G. The invention also discloses a deep - alkali discharge alkaline battery applying the negative zinc paste.
【技术实现步骤摘要】
负极锌膏及耐深度放电碱性电池
本专利技术属于碱性干电池的
，具体地说是涉及一种负极锌膏。本专利技术还涉及一种耐深度放电碱性电池。
技术介绍
碱性电池在使用过程出现漏液是目前碱性电池领域存在的主要问题之一，而中小电流深度放电所引起的电池内部短路是造成碱性电池使用过程出现漏液问题的一个主要原因。目前市场上的碱性电池，在小电流用电器使用过程中经常会出现漏液问题，如遥控器、门铃、剃须刀等，这些用电器的所需工作电流较小，电池使用的时间较长，人们一般不会经常去更换这些电池，往往在发现用电器不能工作时才想起去更换，此时经常会发现电池已经漏液，其实电池已被过度使用，即电池深度放电。而在电池深度放电时，电池负极的锌合金材料容易生成枝晶物质，该枝晶物质会刺穿正负极之间的隔离纸，从而造成电池内部短路，此时电池的正极严重膨胀造成电池内部气压加大，密封圈的安全阀破裂，最终导致电池漏液。目前，碱性电池行业所使用的负极锌粉合金材料，普遍含有铝成分，该成分虽然对电池的大电流放电性能及电池内部气体量抑制方面有所帮助，但对电池在中小电流长时间间歇放电时，更容易产生枝晶物质而造成电池内部短路，从...
【技术保护点】
一种负极锌膏，负极锌膏由以下按重量份的组分组成:锌合金粉 66.20份、聚丙烯酸0.23份、聚丙烯酸钠0.46份、氢氧化钾电解液33.11份；其中，锌合金粉由铋、铟、铅以及锌组成，每克锌合金粉中含铋195μg、铟225μg、铅6μg。
【技术特征摘要】
1.一种负极锌膏，负极锌膏由以下按重量份的组分组成:锌合金粉66.20份、聚丙烯酸0.23份、聚丙烯酸钠0.46份、氢氧化钾电解液33.11份；其中，锌合金粉由铋、铟、铅以及锌组成，每克锌合金粉中含铋195μg、铟225μg、铅6μg。2.根据权利要求1所述的负极锌膏，其特征在于：在锌合金粉粒中，粒径300-400μm的锌合金粉的质量百分比为5.0％，粒径150-300μm的锌合金粉的质量百分比27.9％、粒径105-150μm的锌合金粉的质量百分比为23％、粒径75-105μm的锌合金粉的质量百分比为1...
【专利技术属性】
技术研发人员：赵锋良，吴丹，史振华，徐宏磊，张金艳，
申请(专利权)人：浙江飞狮电器工业有限公司，
类型：发明
国别省市：浙江,33