The invention discloses an inner wall putty powder, by weight consists of the following components: 1 to 2 portions of stearic acid polyoxyethylene ester, 1.2 sodium six partial, 1.1 sodium, 0.9 fatty alcohol ether sodium sulfate, 1.5 copies of the ten isomeric alcohol polyoxyethylene ether, 0.5 cerium hydroxide, 3.7 tourmaline negative ion additive, 19 kaolin powder, 29 portions of rice gel powder, 41 portions of white cement. The invention of the interior wall putty powder, good leveling, strong adhesion, good water resistance, high strength, high grinding, acid and alkali corrosion resistance, high temperature resistance, mildew changes, water moisture without peeling, cracking, hollowing, shedding phenomenon, no yellowing, moldy, dark spots.
【技术实现步骤摘要】
内墙腻子粉
本专利技术涉及内墙腻子粉。
技术介绍
现有内墙腻子粉,其流平性、附着力、耐水性、强度、耐打磨性能、耐酸碱腐蚀性能、耐高低温变化性能、耐霉变性能都有待提高,受水受潮后容易出现空鼓、起皮、龟裂、脱落现象,且容易出现发黄、发霉、起黑斑现象。
技术实现思路
本专利技术的目的在于提供一种内墙腻子粉,其流平性好,附着力强,耐水性好,强度高,耐打磨,耐酸碱腐蚀、耐高低温变化、耐霉变,受水受潮后无空鼓、起皮、龟裂、脱落现象,亦无发黄、发霉、起黑斑现象。为实现上述目的,本专利技术的技术方案是设计一种内墙腻子粉,按重量份计由以下组分组成:1~2份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠,0.9份脂肪醇醚硫酸钠,1.5份异构十醇聚氧乙烯醚,0.5份氢氧化铈,3.7份电气石粉负离子添加剂,19份高岭土粉,29份粳米凝胶粉,41份白水泥。优选的,内墙腻子粉,按重量份计由以下组分组成:1份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠,0.9份脂肪醇醚硫酸钠,1.5份异构十醇聚氧乙烯醚,0.5份氢氧化铈,3.7份电气石粉负离子添加剂,19份高岭土粉,29份粳米凝胶粉,41份白水泥。优选的,内墙腻子粉,按重量份计由以下组分组成:2份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠,0.9份脂肪醇醚硫酸钠,1.5份异构十醇聚氧乙烯醚,0.5份氢氧化铈,3.7份电气石粉负离子添加剂,19份高岭土粉,29份粳米凝胶粉,41份白水泥。优选的,内墙腻子粉,按重量份计由以下组分组成:1.2份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠, ...
【技术保护点】
内墙腻子粉,其特征在于,按重量份计由以下组分组成:1~2份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠,0.9份脂肪醇醚硫酸钠,1.5份异构十醇聚氧乙烯醚,0.5份氢氧化铈,3.7份电气石粉负离子添加剂,19份高岭土粉,29份粳米凝胶粉,41份白水泥。
【技术特征摘要】
1.内墙腻子粉,其特征在于,按重量份计由以下组分组成:1~2份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠,0.9份脂肪醇醚硫酸钠,1.5份异构十醇聚氧乙烯醚,0.5份氢氧化铈,3.7份电气石粉负离子添加剂,19份高岭土粉,29份粳米凝胶粉,41份白水泥。2.根据权利要求1所述的内墙腻子粉,其特征在于,按重量份计由以下组分组成:1份硬脂酸聚氧乙烯酯,1.2份六偏磷酸钠,1.1份烷基苯磺酸钠,0.9份脂肪醇醚硫酸钠,1.5份异构十醇聚氧乙烯醚,0.5份氢氧化铈,3.7份电气石粉负离子添加剂,19份高岭土粉,29份粳米凝胶粉,41份白水泥。3.根据权...
【专利技术属性】
技术研发人员:范毓明,
申请(专利权)人:常熟市奇越新型建材科技有限公司,
类型:发明
国别省市:江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。