The invention relates to a caulking agent, belonging to the technical field of building materials. A sealing agent, which is characterized in that: made of the following raw materials in weight portion: calcium carbonate powder 35-50 parts, white cement, 15-30 antibacterial agent 3-12, polishing agent 3-9, dispersible emulsion powder 2-4 parts, mould 1-2, hydroxypropyl methyl cellulose 0.5-1, superplasticizer 0.1-0.4, gypsum powder 2-8 fly ash, 2-8, rubber powder 1-3 parts. Sealing agent of the invention has the characteristics of anti alkali, anti mildew, waterproof, weather and so on, can be widely used for dry and wet parts of the ceramic tile, stone and other building materials gap filling, lasting effect, little affected by environment, can effectively prolong the service life of ceramic tile.
【技术实现步骤摘要】
本专利技术涉及一种填缝剂，属于建筑材料
技术介绍
新房装修时，很多人都喜欢DIY，既自己为新房设计。说到装修，那肯定就要用到瓷砖。瓷砖既可以铺到地板上，又可以铺到墙壁上。但铺设完瓷砖后，我们需要注意一个问题，那就是瓷砖间会存在一定的缝隙。如今应对这些缝隙的普遍方法就是在缝隙间用上填缝剂。目前，瓷砖饰面所用的填缝剂大多是采用普通水泥、建筑细砂、无机颜料经混合包装，使用时加水调和作为瓷砖缝的填充材料，应用这种瓷砖填缝剂施工完成后不长的时间经风吹、日晒、雨淋、冻融等的自然环境因素的影响下，收缩裂缝、霉变、甚至瓷砖脱落等质量问题和安全隐患。
技术实现思路
本专利技术的目的在于解决上述填缝剂的不足，提供一种效果持久、受环境影响小的填缝剂。本专利技术的一种填缝剂是通过以下技术方案实现的：一种填缝剂，采用如下重量份的原料制成：重钙粉35-50份、白水泥15-30份、抗菌剂3-12份、抛光剂3-9份、可分散乳胶粉2-4份、防霉剂1-2份、羟丙基甲基纤维素0.5-1份、减水剂0.1-0.4份、石膏粉2-8份、粉煤灰2-8份、橡胶粉1-3份。优选的，重钙粉45份、白水泥20份、抗菌剂8份、抛光剂5份、可分散乳胶粉3份、防霉剂2份、羟丙基甲基纤维素0.5份、减水剂0.1份、石膏粉6份、粉煤灰6份、橡胶粉2份。本专利技术的填缝剂，具有抗碱、抗霉、防水、耐候等特点，可广泛用于干燥和潮湿部位的瓷砖、石材以及其它建材缝隙的填充，效果持久，受环境影响小，有效的延长了瓷砖的使用寿命。具体实施方式以下通过实施例形式，对本专利技术的上述内容再作进一步的详细说明，但不应将此理解为本专利技...
【技术保护点】
一种填缝剂，其特征在于：采用如下重量份的原料制成：重钙粉 35‑50份、白水泥 15‑30份、抗菌剂3‑12份、抛光剂3‑9份、可分散乳胶粉 2‑4份、 防霉剂 1‑2份、羟丙基甲基纤维素 0.5‑1份、 减水剂0.1 ‑ 0.4份、石膏粉 2‑8份、 粉煤灰2‑8份、橡胶粉 1‑3份。
【技术特征摘要】
1.一种填缝剂，其特征在于：采用如下重量份的原料制成：重钙粉35-50份、白水泥15-30份、抗菌剂3-12份、抛光剂3-9份、可分散乳胶粉2-4份、防霉剂1-2份、羟丙基甲基纤维素0.5-1份、减水剂0.1-0.4份、石膏粉2-8份、粉煤灰2-8份、橡...