本发明专利技术公开了一种用于汽车滤清器的NBR材质特殊改性密封材料，其材料配方组成以重量份计包括：JSR N220SH生胶100份，碳黑50‑70份，A8000 10‑20份，氧化锌5‑8份，硬脂酸1‑2份，PEG40001 ‑2份，防老剂OCD 2‑}‑3份，VC‑4CC 1‑2份，TRIM/S 3‑5份，S‑80 0.1‑0.5份，本发明专利技术用于汽车滤清器的NBR材质特殊改性密封材料满足国标HG/T4392‑2012，要求硬度70+/‑5SHA，高低温‑50℃~+125℃，耐车用润滑油及燃油如5W40,FUELB等，极低的高温压缩永久变形≤25%（125℃X70h)。

NBR material special modified sealing material for automobile filter

The invention discloses a special modified sealing material for automobile filter NBR material, its material composition by weight: JSR N220SH were 100, 50 carbon black 70, A8000 10 Zinc Oxide 5 20 copies, 8 copies, 2 copies of stearic acid 1, PEG40001 2, antioxidant OCD 2} 3, VC 4CC 1 2, TRIM/S 3 5, S 80 0.1 0.5 copies, the invention is used for automobile filter material NBR modified sealing materials to meet the national standard HG/T4392 2012, hardness 70+/ 5SHA level requirements. Temperature of 50 DEG ~+125 DEG, resistance of vehicle lubricating oil and fuel oil such as 5W40, FUELB, compression permanent deformation is less than or equal to 25% very low temperature (125 degrees X70h).

【技术实现步骤摘要】

本专利技术涉及汽车材料制备领域，具体是一种用于汽车滤清器的NBR材质特殊改性密封材料。
技术介绍
车用滤清器分机油滤清、燃油滤清和空气滤清，主要作用是分离发动机进气过程中的油气杂质、灰尘颗粒，以保护发动机活动部件免受磨损。滤清器密封垫片作为关键部件要求它耐受高低温以满足不同地域使用，长期承压永久变形小以及根据使用场合不同能抗受机油燃油侵蚀。
技术实现思路
本专利技术的目的在于提供一种用于汽车滤清器的NBR材质特殊改性密封材料，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种用于汽车滤清器的NBR材质特殊改性密封材料，其材料配方组成以重量份计包括：JSRN220SH生胶100份，碳黑50-70份，A800010-20份，氧化锌5-8份，硬脂酸1-2份，PEG40001-2份，防老剂OCD2-

【技术保护点】
一种用于汽车滤清器的NBR材质特殊改性密封材料，其特征在于，其材料配方组成以重量份计包括：JSR N220SH生胶100份，碳黑50‑70份，A8000 10‑20份，氧化锌5‑8份，硬脂酸1‑2份，PEG40001 ‑2份，防老剂OCD 2‑3份，VC‑4CC 1‑2份，TRIM/S 3‑5份，S‑80 0.1‑0.5份。

【技术特征摘要】
1.一种用于汽车滤清器的NBR材质特殊改性密封材料，其特征在于，其材料配方组成以重量份计包括：JSRN220SH生胶100份，碳黑50-70份，A800010-20份，氧化锌5-8份，硬脂酸1-2份，PEG40001-2份，防老剂OCD2-3份，VC-4CC1-2份，TRIM/S3-5份，S-800.1-0.5份。2.根据权利要求1所述的一种用于汽车滤清器的NBR材质特殊改性...