The invention discloses a high-efficiency antistatic coating, which comprises the following components: weight matrix resin 60 ~ 80, 40 ~ 60 acrylate polymer emulsion, polyisocyanate curing agent, 5 to 8, 5 to 12 portions of carbon nanotubes and nano silicon dioxide from 5 to 10, heavy calcium carbonate - 15, 10 graphite powder 3 ~ 5, 2 ~ 4 wetting agent and coupling agent 3 - 5, methyl ethyl ketoxime 0.5 ~ 1.5, 5 ~ 10 film-forming agent, leveling agent 3 ~ 5. The invention relates to a high-efficiency antistatic coating, through the reasonable formula design, the antistatic coating obtained in antistatic agent is relatively small (carbon nanotube) dosage, has excellent antistatic properties, mechanical properties of the coating and the excellent and broad application prospect.
【技术实现步骤摘要】
本专利技术涉及涂料领域，特别是涉及一种高效抗静电涂料。
技术介绍
抗静电涂料是具有导电和排除积累静电荷能力的功能性涂料。目前，工业应用中最常用的抗静电改性方法为添加抗静电剂或使用抗静电填料。抗静电剂使用方面，但其抗静电性能差，持久性不足；而最常用的抗静电填料是炭黑，其缺点是所需要的添加量太大，颜色较深，对于浅色的涂料产品不适用。
技术实现思路
本专利技术主要解决的技术问题是提供一种高效抗静电涂料，能够解决现有抗静电涂料存在的上述问题。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种高效抗静电涂料，包括如下重量份组分：基体树脂60～80份、丙烯酸酯聚合物乳液40～60份、碳纳米管5～12份、纳米二氧化硅5～10份、重质碳酸钙10～15份、石墨粉3～5份、润湿剂2～4份、偶联剂3～5份、甲乙酮肟0.5～1.5份、成膜剂5～10份、流平剂3～5份。在本专利技术一个较佳实施例中，所述基体树脂为有机氟环氧树脂、有机硅环氧树脂和氨基树脂以3～5：2～3：1的比例混合的混合物。在本专利技术一个较佳实施例中，所述碳纳米管为多壁纳米管，其直径为10～35nm，长度为5～15μm。在本专利技术一个较佳实施例中，所述多壁纳米管的层数为5～12层。在本专利技术一个较佳实施例中，所述润湿剂为聚氧化乙烯烷化醚类或大豆卵磷脂；所述偶联剂为含氨基的硅烷偶联剂。本专利技术的有益效果是：本专利技术一种高效抗静电涂料，其通过合理的配方设计，使得所得的抗静电涂料在相对较小的抗静电剂（碳纳米管）的用量...
【技术保护点】
一种高效抗静电涂料，其特征在于，包括如下重量份组分：基体树脂60～80份、丙烯酸酯聚合物乳液40～60份、碳纳米管5～12份、纳米二氧化硅5～10份、重质碳酸钙10～15份、石墨粉3～5份、润湿剂2～4份、偶联剂3～5份、甲乙酮肟0.5～1.5份、成膜剂5～10份、流平剂3～5份。
【技术特征摘要】
1.一种高效抗静电涂料，其特征在于，包括如下重量份组分：基体树脂60～80份、丙烯酸酯聚合物乳液40～60份、碳纳米管5～12份、纳米二氧化硅5～10份、重质碳酸钙10～15份、石墨粉3～5份、润湿剂2～4份、偶联剂3～5份、甲乙酮肟0.5～1.5份、成膜剂5～10份、流平剂3～5份。
2.根据权利要求1所述的高效抗静电涂料，其特征在于，所述基体树脂为有机氟环氧树脂、有机硅环氧树脂和氨基树脂以3～5...