一种水泥沥青砂浆及其配制方法技术

本发明专利技术公开了一种ＣＡ砂浆及其配制方法，属于建筑材料及其配制工艺技术领域，含有水泥、砂、乳化沥青和水，还含有混合料和铝粉，所述原材料按一定配比和一定投放顺序、一定的拌和工艺配制而成并且制成的ＣＡ砂浆还要达到相应的技术指标要求；本发明专利技术的ＣＡ砂浆用于轨道板和底座基础之间的接合，可以使得轨道板和底座基础严密接合，具有调整和缓冲作用，同时使得轨道具有一定的弹性，从而可增强轨道的使用寿命；本发明专利技术所述的ＣＡ砂浆适用于温暖地区。

Cement asphalt mortar and preparation method thereof

The invention discloses a CA mortar and a preparation method thereof, belonging to the technical field of building materials and its preparation process, containing cement, sand, emulsified asphalt and water containing mixture and aluminum powder, the raw material according to certain proportion of CA mortar and put in order, the mixing process with prepared and made more to meet the requirements of the technical indexes of the CA; the mortar for bonding between slab and base, can make the track plate and the base has a tight connection, and adjust the buffer, and the track has certain elasticity, which can enhance the service life of the track; CA mortar of the present invention is suitable for warmth area.

【技术实现步骤摘要】

本专利技术涉及一种建筑材料及其配制工艺，具体涉及一种砂浆及其配制方法。
技术介绍
随着社会的发展，高速铁路运输已经成为世界各国共同追求的目标。为了适应高速铁路的高平稳性、高耐久性、舒适性的要求，需要采用和发展少维修的无碴轨道。板式无碴轨道采用的钢轨直接安装在轨道板上，轨道板铺设在钢筋混凝土底座基础上。由于底座基础和轨道板都是钢筋混凝土浇筑而成，两者不能直接密贴接合，因此，需要在底座基础和轨道板之间加调整层，使得两者严密接合。
技术实现思路
本专利技术的目的在于提供一种具有调整、弹性和缓冲性能的水泥沥青砂浆，本专利技术的另一目的为提供该水泥沥青砂浆的配制方法。本专利技术的技术方案是一种水泥沥青砂浆，含有水泥、砂、乳化沥青和水，其基本配比如下(按重量份计)水泥325～400，砂 600～700，乳化沥青450～500，水 84.5～120。还含有混合料和铝粉，按重量份计，其配比如下混合料 1.5～2，铝粉0.05～0.06；该砂浆的技术指标要求为抗压强度1天为0.1MPa；7天为0.7MPa；28天为1.8～2.5MPa弹性模量100～300MPa砂浆温度5～30℃流动度 16～本文档来自技高网...

【技术保护点】
一种ＣＡ砂浆，其特征在于：含有水泥、砂、乳化沥青和水，按重量份计，其基本配比如下：水泥３２５～４００，砂６００～７００，乳化沥青４５０～５００，水　８４．５～１２０。还含有混合料和铝粉 ，按重量份计，其配比如下：混合料１．５～２，铝粉０．０５～０．０６；该砂浆的技术指标要求为：抗压强度１天为０．１ＭＰａ；７天为０．７ＭＰａ；２８天为１．８～２．５ＭＰａ弹性模量１００～ ３００Ｍ...

【技术特征摘要】

【专利技术属性】
技术研发人员：钱振地，江成，肖俊恒，刘振民，王智勇，吴海涛，张雷，白昆华，吴利清，杨先凤，王江，张志红，龚斯昆，
申请(专利权)人：中铁八局集团有限公司，
类型：发明
国别省市：90[中国|成都]