Civil engineering materials curing agent and preparation method of the invention is water reducing agent, antifreeze, anti permeability agent, sodium silicate, sodium hydroxide, sodium chloride, maleic acid, ferrous sulfate, sodium phosphate, sodium carbonate, anhydrous sodium sulfate, triethanolamine, calcium silicate and quartz sand adding ball mill grinding, temperature control in 60 to 120 DEG C, grinding fineness 280 ~ 350 mesh, color yellow, bagging standby; then, the mixture of cement lime powder and a step from 2 to 10% while adding ball mill for grinding, the temperature control at 60 to 120 DEG C, the grinding fineness is larger than 200 mesh, pale color, i.e. the finished building materials curing agent. The advantages are: high consolidation strength and water stability and good features, good frost resistance, small deformation, high durability and suitability and wide range, can be the most cheap, ash soil consolidation into to meet the requirements of building materials, can be widely used in water conservancy and Hydropower Engineering, traffic engineering etc..
【技术实现步骤摘要】
本专利技术属于固化剂，特别涉及一种。
技术介绍
目前，土木建筑工程应用的胶凝材料主要是硅酸盐水泥，这种胶凝材料是以砂石料作骨料，对泥土固化效果不好，对水质要求也高。当用沙石作骨料，用硅酸盐水泥作胶凝材料拌合混凝土料时，为不了不影响混凝土的性能，除对砂石料和水质的特殊要求外，则要把砂石中的泥土尽量清洗干净。这不仅费时费力，而且在无砂石料或水质不好的地区，混凝土工程造价将成倍提高。我国幅员辽阔，经、纬度跨度大，北方严寒、南方炎热多雨，各地的土质、气候条件也千差万别，因此寻求一种高强、耐水、适应性强，既可和水泥一样以砂、石碎屑为骨料，又对拌合水质无特殊要求，且能充分利用当地的水土资源，特别是能够固化泥土的水硬性胶凝材料—土壤固化剂。虽然也有土壤固化剂的相关报道，但现有的固化剂在使用过程中出现强度低、抗冻性能差、成本高等问题。因此研制一种使工期最短、施工费用最低，工程质量最优的土壤固化剂是十分必要的。
技术实现思路
本专利技术的目的旨在于提供一种价格低廉能在各种地区与各类土壤发生反应、可利用各种固体废渣废料、筑成稳固持久的建筑构件的新型土壤固化剂。通过按一定比例与土壤拌合...
【技术保护点】
土建材料固化剂，是包括减水剂、抗冻剂、抗渗剂、硅酸钠、氢氧化钠、氯化钠、马来酸、硫酸亚铁、磷酸钠、碳酸钠、无水硫酸钠、三乙醇胺、硅酸钙、石英砂、水泥和生石灰粉混合而成，其混配组份的重量份数为：减水剂０．５～１５份、抗冻剂０．３～７份、抗渗剂０．３～７份、硅酸钠０．５～６份、氢氧化钠０．５～５份、氯化钠０．８～１２份、马来酸０．５～８份、硫酸亚铁１～１５份、磷酸钠０．５～８份、碳酸钠０．５～７份、无水硫酸钠３～２０份、三乙醇胺１～１５份、硅酸钙０．２～８份、石英砂０．３～８份、水泥２０～７５份和生石灰粉３～７５份。
【技术特征摘要】