一种半透明陶瓷砖及其制备方法技术

本发明专利技术公开了一种半透明陶瓷砖及其制备方法，采用了类似于天然翡翠成分的高钠、低钾成分的钠长石质陶瓷配方体系并烧结而成，其方法主要技术特征是将混料原料加水球磨，通过压机设备成型陶瓷砖坯，在成型过程中采用布料等方式加以装饰，并将砖坯放入干燥窑内干燥，在釉线上加以印花或施釉的装饰手法，入辊道窑内烧成，并进行磨边、抛光等冷加工，分选、包装为成品。本发明专利技术在普通墙地砖陶瓷窑炉生产条件下烧制半透明陶瓷砖，填补了国内市场上还没有具有透光性能的高档建筑装饰材料的空白，具有良好的推广价值。

Semi transparent ceramic brick and preparation method thereof

The invention discloses a translucent ceramic tile and preparation method thereof, using high sodium and low potassium components similar to natural jadeite component of sodium feldspathic ceramic formula system and sintering, the main technical features of the method is that the mixing of raw materials with ball milling, the press equipment type of ceramic tile, in the molding process the cloth to decorate, and the tiles into dry kiln drying, to stamp in the glaze line or glaze decoration inside the roller kiln firing, and grinding and polishing processing, sorting and packing. The present invention in ordinary tiles fired ceramic kiln production conditions, translucent ceramic brick, to fill the gaps in the domestic market is not high-grade decoration material with transparent performance, and has good popularization value.

【技术实现步骤摘要】

【技术保护点】
一种半透明陶瓷砖，其特征在于，该半透明陶瓷砖有半透明层，该半透明陶瓷层采用类似于天然翡翠成分（ＮａＡｌ［Ｓｉ２Ｏ６］）的高钠、低钾成分的钠长石质陶瓷配方，具有多种晶体结构及玻璃相，其化学成分按比重百分比计包括：Ｎａ↓［２］Ｏ＞５．２％、Ｋ↓［２］Ｏ＜０．６％、ＳｉＯ↓［２］６２～６９％、Ａｌ↓［２］Ｏ↓［３］２２～２６％、Ｆｅ↓［２］Ｏ↓［３］＋ＴｉＯ↓［２］＜０．６％、ＣａＯ＋ＭｇＯ＜２．２％。

【技术特征摘要】

【专利技术属性】
技术研发人员：唐奇，
申请(专利权)人：佛山欧神诺陶瓷有限公司，
类型：发明
国别省市：44[中国|广东]