The invention relates to a production method of building materials; which is characterized in that the materials were divided into 3540%: fly ash, lime shale 30-35%, 20-25%, 47% coal; compared with the prior art, make full use of the local thermal power plant, chemical plant from fly ash and lime slag cement admixture, turning waste into treasure at the same time, governance, purifying the environment; calcined brick after cooling, loose texture, easily broken, grindability, mill output can be increased by 20 - 30%, saving power consumption, reduced 25 - 30 yuan more than ordinary cement cost per ton; the same ratio, under the same conditions of concrete, its strength and resistance with better than ordinary portland cement; change the content, can produce a variety of volcano ash Portland cement strength grade, suitable for building materials Treatment of waste residue by factories and thermal power plants and chemical plants.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料的生产方法。工业生产中，热电厂排出的粉煤灰渣和化工厂及石灰生产业中排出的生石灰渣是环境治理中的两大公害。本专利技术的目的是利用当地热电厂、化工厂排出的粉煤灰和石灰渣生产水泥混合材，既治理、净化环境，又变废为宝，生产出价廉、质优的建筑材料。本专利技术的目的是这样实现的，材料的组分为粉煤灰35-40％，页岩30-35％，生石灰20-25％，煤炭4-7％。生产工艺过程为(1)配制混合材，将生石灰、页岩、煤炭按比例混合，经粉碎加工后，与粉煤灰一起输入搅拌机里搅拌均匀，含水率达8-12％，再输送到消化仓消解3小时以上；(2)将混合材掺水再次搅拌均匀，含水率达18-25％，用压砖机压制成砖坯；(3)将砖坯装入窑内，先300-400℃以下烘干12小时，再在800℃-950℃温度条件下煅烧24小时，自然温度下冷却1-2小时，即制得高活性混合材；(4)将制得的高活性混合材破碎加工后与50-65％的水泥熟料混合送入磨机磨成粉末材料。本专利技术充分利用了当地热电厂、化工厂排出的粉煤灰和石灰渣生产水泥混合材，变废为宝的同时又治理、净化了环境；煅烧后的砖，冷却后质地疏松，容易破碎，易磨性好，磨机产量可提高20-30％，节省耗电，比普通水泥的吨成本降低25-30元；同配比、相同条件下配制的混凝土，其强度及抗掺性优于普通硅酸盐水泥；改变其掺量，可生产出多种强度等级的火山灰硅酸盐水泥，适宜建材厂和热电厂及化工厂处理废渣治理环境应用。本专利技术以下将结合实施例进一步描述实施例取热电厂排出的粉煤灰5吨，页岩4吨，生石灰3吨，煤炭800Kg，将生石灰、页岩、煤炭...
【技术保护点】
用工业废渣生产水泥混合材的方法，其特征在于材料的组分为：粉煤灰３５－４０％，页岩３０－３５％，生石灰２０－２５％，煤炭４－７％。
【技术特征摘要】
【专利技术属性】
技术研发人员：彭玉龙，
申请(专利权)人：上海国冶工程技术有限公司，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。