结合到聚苯乙烯泡沫塑料上的新型可喷涂磷酸盐水泥的组合物和应用制造技术

干混颗粒组合物，包含Ｍｇ和／或Ｃａ的煅烧氧化物、酸式磷酸盐、以及飞灰或等同物，其中所述煅烧氧化物的量是大约１７重量％－大约４０重量％、所述酸式磷酸盐的量是大约２９重量％－大约５２重量％、所述飞灰或等同物的量是大约２４重量％－大约３９重量％，当在所述干混物中加入砂子时，砂子占所述干混物和砂子的组合的大约３９重量％－大约６１重量％。还公开了形成结构件的方法，其中在干混物和砂子中加入大约８－１２磅水的含水浆料。

Composition and application of novel phosphate cement capable of spraying onto polystyrene foam

Dry mixed particle composition, containing Mg and / or Ca calcined oxide, acid phosphate, and fly ash or equivalent, wherein the calcined oxide amount is about 17 wt% and about 40 wt%, the phosphate content is about 29 wt% and about 52 wt%, the fly ash or equivalent amount is about 24 wt% and about 39 wt%, when the dry blend with sand, sand for the dry mix and sand about 39 wt% and about 61 weight%. A method of forming a structural member in which an aqueous slurry of about 8-12 pounds of water is added to the dry mixture and sand.

【技术实现步骤摘要】
【国外来华专利技术】专利技术的合同来源根据U.S.Department of Energy(DOE)和代表Argonne NationalLaboratory的芝加哥大学之间的W-31-109-ENG-38号合同，美国政府享有该专利技术的权益。
技术介绍
本专利技术涉及可泵送的陶瓷，更具体而言，本专利技术涉及可用于建筑业中的陶瓷组合物，其可用于在各种温度条件下将所述陶瓷施加到竖直的墙以及斜墙和水平墙上，比如屋顶，从而提供针对水泥或聚苯乙烯泡沫塑料基底而言便宜的涂料。尤其在加勒比和南美国家，对下述建筑材料有强烈的需求它可以现场混合，施加到基底结构(包括聚苯乙烯泡沫塑料)上，而且可以被加工比如涂抹，但仍然在足够短的时间内固化以至于无需采用机械锚定比如金属丝或其它机构来将制品固定到垂直表面上。发展中国家需要廉价房，尤其是那种能承受热带和亚热带气候的不需熟练技术工而且可以快速建起的廉价房。Agonne国家实验室在开发磷酸盐基水泥或陶瓷产品方面一直处于领先地位，磷酸盐基水泥或陶瓷产品有很广泛的用途，如在1997年7月8日授予Wagh等的美国专利5645518“Method for StabilizingLow-Leve本文档来自技高网...

【技术保护点】
干混颗粒组合物，包含Ｍｇ和／或Ｃａ的煅烧氧化物、酸式磷酸盐以及飞灰或等同物，其中所述煅烧氧化物的量是大约１７重量％－大约４０重量％、所述酸式磷酸盐的量是大约２９重量％－５２重量％、所述飞灰或等同物的量是大约２４重量％－大约３９重量％。

【技术特征摘要】
【国外来华专利技术】...

【专利技术属性】
技术研发人员：AS沃格，JW小保罗，
申请(专利权)人：芝加哥大学阿尔贡有限责任公司，
类型：发明
国别省市：US[美国]