Reflection broken mirror artificial stone, crushed into particles of different sizes as the main filler with single or double glass mirror, according to the design of color color dye trace particles, adding unsaturated polyester adhesive, adhesive and filler mixing ratio of 1: 1 - 10Kg, create a reflection broken mirror artificial stone. The manufacturing process is: 1. packing: manufacturing finished mirror single or double break, put grinding machine, according to the design requirements, produce a single mirror or double mirror broken particles according to the production needs of broken particles of different sizes. 2. according to the design color, add color particles, put the mixer, mixing, mixing evenly. Adding 3. unsaturated polyester adhesive, adhesive and filler weight is the total weight of 10 to 50%. 4. of the raw materials are evenly mixed according to certain ratio, molding, demoulded, dried and polished to produce reflection broken mirror artificial stone. The artificial stone is more beautiful and diverse, and can also make all kinds of art glass in the same way.
【技术实现步骤摘要】
本专利技术涉及一种Aiit石材料组成成分及制造工艺，尤其涉及一种反光型碎镜人 造石及其制造工艺。
技术介绍
现代建筑材料的发展，对建筑材料要求具有美观多样性、高强度、轻质量執寺点，Ait石具有花纹图案多样性，可由设计者自行控制确定，高^it耐腐蚀，无放 射性，质量轻，点，已经成为广泛应用的建筑材料之一。目前，市场上Aii石组 成成分及制itX艺，多采用聚脂型Ait石，这种Ait石，主要是由黏合剂和填料组 成，黏合剂是不饱和聚脂，填料主要有石英沙、大理石、方解石粉、粉碎的废旧普 通玻璃，两者按一定比例均匀混合后，浇铸成型，经过脱膜、烘干、抛光而成。其 不^处是在光亮处没有5^斑斓的反光和光线折射功能。
技术实现思路
本专利技术的目的在于，克服现有技术的不^处，提供一种可在光线照射下，具 有彩色反光效果的一种反光型碎镜Ait石及其制造工艺。本专利技术所述的一种反光型碎镜Ait石，M用单面或双面玻璃镜粉碎成不同大 小颗粒，作为主要填充料，并按设计色彩加入微量色彩颗粒染料，再加入不饱和聚 脂黏合剂，而制造成一种反光型碎镜A3t石，它可以通过碎H^粒反光、折光原理 形成五彩...
【技术保护点】
反光型碎镜人造石，其特征在于采用单面或双面玻璃镜粉碎成不同大小的颗粒，作为主要填充料，并按设计色彩加入微量色彩颗粒染料，再加入不饱和聚脂黏合剂而制成，通过以下措施来达到：一种反光型碎镜人造石的组成成分，由碎镜填料和不饱和聚脂黏合剂构成，其黏合剂与填料的混合比例为１∶１－１０Ｋｇ。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。