The invention relates to a ceramic manufacturing method, in particular to a method for manufacturing toughened silicon carbide ceramics. The invention provides a method for manufacturing a flake alumina particle combined carbon fiber composite toughening silicon carbide ceramic. Different from pure carbon fiber to toughen the scheme, the characteristic of this invention, is to replace part of the carbon fiber is difficult to be mixed with flaky alumina particles, so as to weaken the negative effect caused by inhomogeneous material mixing, the scheme of the invention is combined with the combination of silicon carbide ceramic toughening, with flake aluminum oxide particles and carbon fibers and flaky alumina grain easily with other raw materials mixed evenly. The scheme of the invention takes into account both the advantages of using thermal expansion mismatch to induce micro cracks, crack deflection, crack bridging, sheet toughening, particle pulling out effect, and carbon fiber pull out effect, and other beneficial toughening factors.
【技术实现步骤摘要】
本专利技术涉及陶瓷制造技术，是关于碳化硅陶瓷制造技术，特别是关于一种 。碳化硅陶瓷材料具有高温强度大、高温抗氧化性强、耐磨损性能好、热稳 定性佳、热膨胀系数小、热导率大、硬度高、抗热震和耐化学腐蚀等优良特性， 在汽车、机械化工、环境保护、空间技术、信息电子、能源等领域有着日益广 泛的应用，已经成为一种在很多工业领域性能优异的其他材料不可替代的结构 陶瓷。机械设备中的动密封是通过两个密封端面材料的旋转滑动而进行的，作为 密封端面材料，要求硬度高，具有耐磨损性。碳化硅陶瓷的硬度相当高且摩擦 系数小，故碳化硅陶瓷作为机械密封端面材料可获得其它材料所无法达到的滑 动特性。另一方面，两个端面密封材料在旋转运动过程中由于摩擦会产生一定 的热量，从而使密封端面的局部温度升高，因此端面材料还必须能够耐受一定 的温度。为了避免端面密封材料在旋转滑动过程中产生热应变和热裂，要求端 面材料的导热系数高、抗热震性好。目前，碳化硅陶瓷已经在各类机械密封中 获得大量的应用，并为机械设备的省力和节能做出了很大的贡献，显示出其他 材料所无法比拟的优越性。碳化硅陶瓷在机械工业中还被成功地用作各种轴...
【技术保护点】
一种片状氧化铝颗粒结合炭纤维组合增韧碳化硅陶瓷制造方法，该制造方法的主要原料是碳化硅粉、烧结助剂、增韧料以及结合剂，经混合、成型、固化、高温烧结等主要工艺步骤，形成碳化硅陶瓷产品，所述碳化硅粉的成份是碳化硅晶粒，原料中含有的增韧料是为增加碳化硅陶瓷的韧性而加入的物料，所述高温烧结工艺步骤的烧结方式是无压固相烧结或无压液相烧结，其特征在于，所采用的增韧料是由片状氧化铝颗粒和炭纤维两种原料构成，所述片状氧化铝颗粒是颗粒形貌呈片状的氧化铝粉。
【技术特征摘要】
【专利技术属性】
技术研发人员：李榕生，水淼，王霞，宋岳，
申请(专利权)人：宁波大学，
类型：发明
国别省市：97[中国|宁波]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。