The invention relates to a high efficiency absorbing ceramic matrix material and a preparation method thereof, which is characterized in that one end of the ceramic base material for the transparent layer, the other end is a reflection layer, the middle is absorbing the at least one layer; the preparation process is as follows: first, the preparation of ceramic slurry, then with the continuous carbon fiber (C: F) impregnated into the slurry to hang pulp, made of a size C: P ceramic blank, and the bottom in the graphite mold; after adding carbon nanotubes (CNTs) / ceramic powder, hot press sintered layered material impedance transition. Influence of this method on the performance of CNTs itself is very small; arrangement of different directions: C f can eliminate the anisotropy and further improve the overall mechanical properties of materials; a hot press molding the multilayer material, has the advantages of simple process, low production cost.
【技术实现步骤摘要】
本专利技术是关于，属于功能 复合材料
技术介绍
碳纳米管具有独特而优异的力学和物理性能(Popov VN， Mater Sci Eng R 2004, 43: 61-102; Lau KT, Hui D, Compos Part B Eng 2002, 33: 263-277)，因 而如何充分利用它的这些性能成了研究的热点。制备碳纳米管复合材料是切 实可行的方法之一。宁金威等曾报道了具有微波吸收功能的碳纳米管/陶瓷复 合材料及制备方法(宁金威，张俊计，潘裕柏，黄莉萍，郭景坤，邱发贵， ZL: 03129563.0)。向长淑等采用快速溶胶-凝胶法制备复合粉体，热压烧结 后制备的碳纳米管/氧化硅块体复合材料具有优异的微波衰减性能(Xiang CS, Pan YB, Liu XJ, Sun XW， Shi XM, Guo JK, Appl Phys Lett 2005, 87(12): 123103)。其进一步研究表明，复合材料的微波衰减性能随着碳纳米管含量的 增加而迅速增强。但是，碳纳米管含量的增加会导致复合材料从绝缘体变成 导体，从而增强了复合材料表面...
【技术保护点】
一种高吸波效率的陶瓷基层状材料，其特征在于所述的陶瓷基层状材料的一端为透波层，另一端为反射层，中间是至少一层的吸波层；所述的透波层为陶瓷层；反射层为碳纤维复合的陶瓷层，或为碳纤维复合的陶瓷层与通过不同排列方式的碳纤维复合的陶瓷层的叠加层；其中碳纤维的质量百分含量１％－８０％，中间梯度吸波层是质量百分含量为Ｘ％的碳纳米管与陶瓷层的复合材料，碳纳米管的质量百分含量从与透波层相邻的吸波层到邻近反射层依次呈梯度渐变增加；且０＜Ｘ≤４５； 所述的陶瓷层为氧化物或非氧化物，氧化物为ＳｉＯ↓［２］、Ａｌ↓［２］Ｏ↓［３］、ＺｒＯ↓［２］或莫来石中一种；非氧化物为Ｓｉ↓［３］Ｎ↓［４］或ＳｉＣ。
【技术特征摘要】
【专利技术属性】
技术研发人员：朱勇，潘裕柏，寇华敏，向长淑，郭景坤，
申请(专利权)人：中国科学院上海硅酸盐研究所，
类型：发明