A building exterior wall thermal insulation putty comprises at least 40 to 55 weight parts of Portland cement and other components, the other components and weight: 20 - 35, quartz silica powder is 15 - 20, 5 - 10, 5 diatomite, sepiolite, perlite, 5 - 10 - 10, cenosphere 5 - 10, 0.5 - 1.5 crack fiber and water reducing agent 0.5 - 1, 1 - 2 polyacrylamide, redispersible polymer powder 3 - 6. The invention of the building exterior wall thermal insulation putty is a comprehensive use of polypropylene fiber, polymer modification technology and insulation material preparation of new building exterior wall putty, not only has good insulation performance and good waterproof performance, and has considerable strength, can be directly used for paint, tile paste, with solid paste, no cracking, insulation, hydrophobicity, characteristics of simple construction.
【技术实现步骤摘要】
本专利技术涉及一种建筑用的墙体保温材料。
技术介绍
建筑物墙体涉及建筑防水和建筑节能保温两个问题,现有的建筑防水材 料和保温材料性能单一,防水的不保温,保温的不防水,有些不能和墙体结 合成一体,强度不好,而且成本高。
技术实现思路
本专利技术的目的是提出一种具有良好保温性能和良好防水性能,并具有强 度的建筑内外墙保温膩子。本专利技术的目的是通过如下的技术方案来完成的,本专利技术的一种建筑内外墙保温腻子至少包括40—55重量份的硅酸盐水泥和其它组份,所述的其它组 份和重量份数为石英沙 20—35硅微粉 15—20海泡石 5—10硅藻土 5 — 10膨胀珍珠岩 5—10空心微珠 5—10抗裂纤维 0.5 — 1.5减水剂 0.5—1聚丙烯酰胺 l一2可再分散聚合物胶粉3—6。本专利技术的建筑内外墙保温膩子是一种综合采用抗裂纤维、聚合物改性技术和绝热材料制备的新型建筑内外墙保温膩子,不但具有良好保温性能和良 好防水性能,并具有相当强度,可直接进行涂料施工,粘贴瓷砖,具有粘贴 牢固,不开裂,隔热,憎水,施工简便的特点。具体实施方式建筑内外墙保温腻子包括40重量份的硅酸盐水泥和其它组份,其它组份和重量份数为石英沙20硅微粉15海泡石5硅藻土5膨胀珍珠岩5空心微珠5抗裂纤维0.5减水剂0.5聚丙烯酰胺1可再分散聚合物胶粉3 Q权利要求1. 一种建筑内外墙保温腻子至少包括40-55重量份的硅酸盐水泥和其它组份,其特征在于所述的其它组份和重量份数为石英沙20-35硅微粉15-20海泡石5-10硅藻土5-10膨胀珍珠岩5-10空心微珠 5-10抗裂纤维 0.5-1.5减水 ...
【技术保护点】
一种建筑内外墙保温腻子至少包括40-55重量份的硅酸盐水泥和其它组份,其特征在于所述的其它组份和重量份数为:石英沙20-35硅微粉15-20海泡石5-10硅藻土5-10膨胀珍珠岩5-10空心微珠5-10抗裂纤维0.5-1.5减水剂0.5-1聚丙烯酰胺1-2可再分散聚合物胶粉3-6。
【技术特征摘要】
【专利技术属性】
技术研发人员:涂国义,俞岷雪,怀彩新,黄春华,
申请(专利权)人:涂国义,
类型:发明
国别省市:33[中国|浙江]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。