本发明专利技术公开了一种人造石面板，是由不饱和聚酯树脂先加入环烷酸钴促进剂、甲乙酮、光稳定剂、颜料和抗氧剂组成，其生产方法是先将氢氧化铝和／或碳酸钙进行改性，得到表面改性氢氧化铝和／或碳酸钙或单纯的氢氧化铝粉，然后在不饱和聚酯树脂先加入环烷酸钴促进剂、甲乙酮、光稳定剂、颜料和抗氧剂，于高速搅拌反应釜中混合搅拌均匀，加入表面改性氢氧化铝和／或碳酸钙粉体或单纯的氢氧化铝粉，搅拌，真空脱泡后浇注于模具中，升温至６０－８０℃固化，即为人造玉石、大理石面板。

Artificial stone panel and manufacturing method thereof

The invention discloses an artificial stone panel is made of unsaturated polyester resin before adding cobalt naphthenate accelerant, methyl ethyl ketone, light stabilizer, antioxidant and pigment composition, its production method is the first modification of aluminum hydroxide and / or calcium carbonate, surface modification of aluminum hydroxide and / or calcium carbonate or pure aluminum hydroxide powder. And then adding cobalt naphthenate accelerant, methyl ethyl ketone, light stabilizers, pigments and antioxidant in unsaturated polyester resin, high speed in stirred reactor mixing, adding surface modified aluminum hydroxide and / or calcium carbonate powder or pure aluminum hydroxide powder, stirring, vacuum deaeration after pouring on the mold, heating to 60 - 80 C is for curing, artificial marble, jade.

【技术实现步骤摘要】

本专利技术涉及一种人造材料，特别是利用非金属矿及有机材料制作的仿石门板、桌面、门 框、窗框、地板或工艺品及其制造方法。技术背景长期以来，人们建造的宾馆、住宅、办公场所和娱乐场所都需要使用大量的木材，除了 墙体和屋顶、柱子或地板使用水泥或石材以外，大量的建筑材料都使用木材金属材料，特别 是门板、桌面、门窗框等，所以我国木材的需求量逐年递增，据统计，这几年，我国每年木 材消耗量都在3亿立方米以上，而根据我国目前自然生态的状况，每年我国政府下达木材釆伐的限额只有1.4立方米；而铝合金、钢材也随着矿产资源的逐渐减少也越来越贵，所以近年来用其它材料代替木材和钢材的研究已经成为我国建材行业的重要手段，其中复合木地 板、人造板、仿石桌面和门窗框等己经成为新兴的木材和钢材的代用品。公开文献报道也一 些这方面的内容，例如题名聚酯型人造大理石的制备作者张丹余海军机构1沈阳化工学院，2沈阳工业大学，刊名辽宁化工.2007，36(2).-86-8文摘以不饱和聚酯树 脂、氢氧化镁、苯乙烯为主要原料，在常压下浇铸制备了人造大理石。研究了氢氧化镁粒度、 氢氧化镁含量以及苯乙烯含量对产品力学性能的影响。结果显本文档来自技高网...

【技术保护点】
一种人造石面板，其特征在于：它是由以下的原料制成的，其质量份数为：　氢氧化铝　２０－７０份；　碳酸钙　０－６０份；　不饱和聚酯树脂　３０－４０份；　甲乙酮　０．５－１．５份；　环烷酸钴　０．５－１．５份；　聚硅氧烷改性剂　０－１份；　光稳定剂，　０．５－１．５份；　抗氧剂　０．５－１．５份；　颜料　适量；　以上所述的氢氧化铝为过２００目的粉末；以上所述的碳酸钙为过５００目的粉末。

【技术特征摘要】

【专利技术属性】
技术研发人员：覃庆峰，
申请(专利权)人：覃庆峰，
类型：发明
国别省市：45[]