微晶玻璃及其生产工艺制造技术

本发明专利技术的微晶玻璃，由二氧化硅５６～５８％、氧化铝１２～１４％、氧化硼２．５～３％、氧化镁５～６％、氧化钙５～６％、氧化锌３．５～４％、氧化锂１．７～２％、氧化钠４．２～４．５％、氧化钾２．８～３．１％、氧化锆２％和氟１．９～２％熔炼制成。其工艺方法是将溶制的玻璃溶液用水淬法急冷，制成基料。将基料装入模具中，进行二次结晶热处理。即在７２０℃分相、在８１０℃核化、在１０５０～１０４０℃晶化，最后在７１０℃下保持６０分钟，消除内应力。用上述工艺可生产出１ｍ↑［２］以上的大规格微晶玻璃。（*该技术在2015年保护过期，可自由使用*）

Glass ceramics and process for producing the same

The glass ceramics of the invention, made from 56 to 58%, silica alumina of 12 ~ 14%, 2.5 ~ 3%, boron oxide, calcium oxide, Magnesium Oxide 5 ~ 6% 5 ~ 6%, 3.5 ~ 4%, Zinc Oxide lithium 1.7 ~ 2%, 4.2 ~ 4.5%, Na2O K2O was 2.8 ~ 3.1%, 1.9 ~ 2% of zirconium oxide and fluoride 2% smelting. The process is to make the soluble glass solution cold quenching and make the base material. The base material is loaded into the mold and subjected to two crystallization heat treatment. That is, at 720 degrees of separation, at 810 degrees nucleation, crystallization at 1050~1040 degrees Celsius, and finally at 710 degrees for 60 minutes, to eliminate internal stress. The process can produce 1m = 2 or more large size glass ceramics.

【技术实现步骤摘要】

本专利技术涉及一种装饰用微晶玻璃的配方和生产方法。目前市售的微晶玻璃，由于没能消除内应力，因此不能生产大块微晶玻璃，超过500mm2以后，会自行炸裂，成品率很低。本专利技术的目的，是提供一种可消除微晶玻璃内应力的微晶玻璃配方和生产工艺。微晶玻璃的配方是二氧化硅(S1O2)56～58％，氧化铝(AL2O3)12～14％，氧化硼(B2O3)2.5～3％、氧化镁(MgO)5～6％、氧化钙(CaO)5～6％、氧化锌(ZnO)3.5～4％、氧化锂(L12O)1.7～2％、氧化钠(Na2O)4.2～4.5％、氧化钾(K2O)2.8～3.1％、氧化锆(ZrO2)2％、氟(F)1.9～2％，百分比按重量计。微晶玻璃生产工艺一、按上述微晶玻璃配方比例，取微晶玻璃原料，经混合后，用电熔炉在1500℃左右高温下熔制。二、将玻璃溶液经水淬法急冷，制成碎颗粒，经筛选、烘干后，制成碎玻璃基料。三、将碎玻璃基料装入设定模具中，进行二次结晶化热处理。其具体工艺是1、分相在温度720℃±10℃下，时间60分钟，使玻璃受控分相。在分相过程中，多种二元系统硅酸盐、氟金云母及网络体外的阳离子进行配位、富集，达到晶前状本文档来自技高网...

【技术保护点】
微晶玻璃，其特征在于该微晶玻璃由二氧化硅５６～５８％、氧化铝１２～１４％、氧化硼２．５～３％、氧化镁５～６％、氧化钙５～６％、氧化锌３．５～４％、氧化锂１．７～２％、氧化钠４．２～４．５％、氧化钾２．８～３．１％、氧化锆２％、氟１．９～２％配制成，百分比按重量计。

【技术特征摘要】

【专利技术属性】
技术研发人员：梁东明，
申请(专利权)人：梁东明，
类型：发明
国别省市：89[中国|沈阳]