The invention relates to a method for manufacturing vacuum glass, which belongs to the technical field of glass product manufacture. Includes the following steps: according to the need to cut a piece of flat glass and a convex glass, and grinding machine according to the need; the film laminated glass plate glass and convex glass edge folding, placed in a glass fixture, into the vacuum laminated furnace, vacuum pumping, heating 13h at 140 to 160 DEG C. temperature, the glass and film fusion; after natural cooling of baked, vacuum glass for sealing sealant protection. The production process of the invention is simple and easy, and is directly connected by the convex glass and the flat glass, so that the support of the two glass hollow region is more stable. Laminated glass film edge seals has the characteristics of heat resistance and cold resistance, high mechanical strength, - 40 DEG C to + 120 DEG C can keep various physical performance and stability. Vacuum glass can be evacuated and sealed in batches to achieve efficient production.
【技术实现步骤摘要】
本专利技术属于玻璃制品制造
，具体涉及。
技术介绍
真空玻璃的传热系数低、隔热隔声性能优良，在一些领域尤其是在建筑门 窗玻璃应用领域有庞大的需求，但有一些技术和工艺不利于工业化快速生产。如专利号200420109208.9的中国专利公开的柔性支撑真空玻璃，中间层采用 支撑物，采用复合玻璃密封胶封口。其产品一般只能用于中空玻璃，玻璃密封 胶类产品使用在真空玻璃的封边结构上，透气率很难保证在10—8pa *L/S级别上。 且由于其在玻璃面上采用抽气装置，其工艺性难以实现高速批量生产。又如专 利号200510069186.7的中国专利公开的建筑真空玻璃板的生产方法，特点是 采用丝网印刷工艺印制围边封接带和中间支承点的焊接玻璃料，其不在玻璃上 使用抽气装置，在真空高温封接工序同时完成玻璃封接与真空腔的形成。这种 方法，要求真空室加热到200—40(TC，焊接工作温度达380—48(TC，极大地耗用能源，也无法使用钢化玻璃进行真空加工。另外，合片、抽真空、封结的工 序全部集中在小小的真空室中完成，这种通过控制机械在真空室将一片一片玻 璃进行组合的方法，生产效率很低。...
【技术保护点】
一种真空玻璃的制造方法，包括以下步骤：（ａ）按真空玻璃的尺寸需要切割一块平板玻璃（２）和一块凸点玻璃（１），并按需要进行磨边加工；（ｂ）采用夹胶玻璃胶片（４）将平板玻璃（２）和凸点玻璃（１）围边叠合，玻璃叠合后成批放置在玻璃夹具上，进入真空夹胶炉，逐步抽真空，在１４０℃－１６０℃温度下，加热１－３ｈ，使玻璃和胶片融合；（ｃ）自然冷却后出炉，按常规技术用保护密封胶对真空玻璃周边进行密封加固。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。