本发明专利技术提供一种光学玻璃，其折射率（ｎｄ）为１．７５以上、阿贝数（ｖｄ）范围为１５～４０、且适于精密模压成型。该光学玻璃，其特性在于：以氧化物为基准的摩尔％，含有１０～７０％的Ｂ↓［２］Ｏ↓［３］＋ＳｉＯ↓［２］、５％以上且未满２５％的Ｂｉ↓［２］Ｏ↓［３］、５～６０％的ＲＯ＋Ｒｎ↓［２］Ｏ（Ｒ表示选自由Ｚｎ、Ｂａ、Ｓｒ、Ｃａ、Ｍｇ所组成的群中的一种以上，Ｒｎ表示选自由Ｌｉ、Ｎａ、Ｋ、Ｃｓ所组成的群中的一种以上）的各成分，且在可见范围的透明性高，转变温度（Ｔｇ）为５２０℃以下，在波长５５０ｎｍ下、１０ｍｍ厚的分光透过率为７０％以上。

optical glass

The invention provides an optical glass with refractive index (nd) of more than 1.75 and Abbe number (VD) range of 15~40, and is suitable for precise molding. The optical glass, the utility model is characterized in that: mol% with oxide as the benchmark, containing 10 to 70% B: 2 O: 3 SiO: 2, above 5% and under 25% Bi: 2 O: 3, 5 ~ 60% RORn: 2 O (R Zn, Ba, said the selected Sr, Ca, Mg group consisting of more than one of Rn, Li, Na, said the selected K, Cs group in more than one) of each component and the transparency of the visible range of high transition temperature (Tg) 520 DEG C, in 550nm, the thickness of 10mm wavelength light transmittance is above 70%.

【技术实现步骤摘要】
【国外来华专利技术】
本专利技术涉及一种光学玻璃，其在可见范围的透明性高、具有折射率(nd) 为1.75以上及阿贝数(vd)范围为15~40的光学常数，且适于精密模压成型。
技术介绍
以前，高折射率、高分散区域的光学玻璃是以大量含有氧化铅的组成体 系为代表的，由于玻璃的稳定性佳，且玻璃的转变温度(Tg)低，因此被作 为用于精密压模成型的玻璃。例如，在专利文献l中公开有大量含有氧化铅 的用于精密模压的光学玻璃。然而，由于实施精密模压成型时的环境，为了防止金属模具的氧化，被 保持在还原性气氛，因此，在玻璃成分中含有氧化铅时，会有从玻璃表面析 出被还原的铅，附着于金属模具表面，无法维持金属模具的精密面的问题。 而且，氧化铅对环境有害，期望实现无铅化。回应此期望，高折射率、高分散区域且不含氧化铅的用于压制成型的光 学玻璃被大量开发，但几乎都是含有高浓度的Nb20s的磷酸盐玻璃。例如， 在专利文献2与专利文献3中公开有P205-Nb205-W03-(K20，Na20，Li20;^的 玻璃、在专利文献4中公开有P205-Nb205-Ti02-Bi203-Na20系的玻璃。然而， 虽说该等玻璃的Tg低，但多为超过48本文档来自技高网...

【技术保护点】
一种光学玻璃，其特征在于：　　　　以氧化物为基准的摩尔％，含有５％以上、未满２５％的Ｂｉ↓［２］Ｏ↓［３］，且折射率（ｎ↓［ｄ］）为１．７５以上，阿贝数（ｖ↓［ｄ］）为１５～４０。

【技术特征摘要】
【国外来华专利技术】...

【专利技术属性】
技术研发人员：傅杰，
申请(专利权)人：株式会社小原，
类型：发明
国别省市：JP[日本]