低固含量的电子布用石蜡型浸润剂制造技术

一种低固含量的电子布用石蜡型浸润剂，包括如下重量百分组成：石蜡１．２～１．５％、机油０．８～１．５％、凡士林０．８～１．５％、乳化剂０．６～０．８％、阳离子软片０．１～０．１５％、固色剂２．５～３．８％和余量的水。配方中还可以加入环氧树脂，占总量的０．３～０．５％。本发明专利技术减少了浸润剂配方中石蜡、凡士林和机油等油类物质的用量，添加了一定比例的阳离子软片。采用这种浸润剂表面涂覆的玻璃纤维纱柔软，纺织性能好，并且可燃物含量低。经过实际检测用这种配方生产的玻璃纤维纱的可燃物含量为０．７５％－０．８５％，较原先石蜡纱的可燃物含量１％降低了１５％－２５％，并降低了生产成本。

Low solid content electronic cloth, paraffin type wetting agent

Paraffin sizing material for an electronic cloth of low solid content, including the following components: 1.2 weight% ~ 1.5%, paraffin oil 0.8 ~ 1.5%, 0.8 ~ 1.5%, Vaseline emulsifier is 0.6 ~ 0.8%, 0.1 ~ 0.15%, cationic film fixing agent 2.5 ~ 3.8% and the balance of water. Formula can also be added epoxy resin, accounting for 0.3 to 0.5% of the total. The invention reduces the amount of oil, such as paraffin, vaseline and oil, in the formula of wetting agent, and adds a certain proportion of cationic film. The glass fiber yarn coated with this soakage agent is soft, good in textile property and low in fuel content. Through the actual test using this formula, the production of glass fiber yarn combustible content is 0.75% - 0.85%, 1% higher than the original content of combustible paraffin yarn is reduced by 15% - 25%, and reduced the cost of production.

【技术实现步骤摘要】

本专利技术涉及一种低固含量的改性石蜡型玻璃纤维浸润剂配方，特别适合用于生产织 造电子布使用的单丝直径为9微米的连续型无碱玻璃纤维纱。
技术介绍
目前，公知的玻璃纤维石蜡型浸润剂配方中的润滑组分全部采用石蜡、凡士林、机 油或变压器油等油类物质。这种玻璃纤维浸润剂的固含量高，造成拉制的玻璃纤维纱的 浸润剂含量在1%以上。用这种玻璃纤维纱织造的电子布，使用以前需要将布面上浸润剂 全部用高温焖烧，在焖烧的过程中耗用了大量的的电能。并且由于玻璃纤维纱的浸润剂 含量高造成了焖烧后的布面浸润剂残留较高，影响了下一道工序的使用效果。
技术实现思路
本专利技术所要解决的技术问题是提供一种低固含量的电子布用石蜡型浸润剂，克服现 有的石蜡型浸润剂配方固含量高、织造的电子布在焖烧去除浸润剂时残留量高而且耗用 时间长的不足。本专利技术低固含量的电子布用石蜡型浸润剂，其特征在于包括如下重量百分组成 石蜡1.2~1.5%、机油0.8~1.5%、凡士林0.8~1.5%、乳化剂0.6~0.8%、阳离子软片 0.1~0.15%、固色剂2.5~3.8%和余量的水。配方中还可以加入环氧树脂，占总量的0.3~0.5%。本专利本文档来自技高网...

【技术保护点】
一种低固含量的电子布用石蜡型浸润剂，其特征在于包括如下重量百分组成：石蜡１．２～１．５％、机油０．８～１．５％、凡士林０．８～１．５％、乳化剂０．６～０．８％、阳离子软片０．１～０．１５％、固色剂２．５～３．８％和余量的水。