A flame retardant woven rattan handicraft processing method, relates to the weaving technology field, which comprises the following steps, rattan, rattan, playing pick wash rattan, peeling, soaking and drying, the immersion is the soaking liquid, the liquid comprises the following components according to weight, iodine 0.4 ~ 0.6, PVP 0.8 - 1, 0.4 - 0.6, ethanol ether 2 ~ 3, 80 ~ 120 copies of pure water and bentonite 2 ~ 3. The invention can prevent the cane from damp and moldy, is not easy to produce insects, has good flame retarding effect and high strength, and increases the service life of the knitting fabric.
【技术实现步骤摘要】
:本专利技术涉及编织工艺
,具体是一种阻燃的工艺品编织藤条处理方法。
技术介绍
:在藤条编织工艺品前,一般会对藤条进行一些特殊的处理,一般包括软化、增强韧性、去皮等处理,现有技术中由于藤条的材质问题,藤条编织的工艺品容易吸潮,导致其发霉或者生虫腐烂等,使用寿命低。
技术实现思路
:本专利技术所要解决的技术问题在于提供一种防止藤条受潮发霉,增加编织品使用寿命的阻燃的工艺品编织藤条处理方法。本专利技术所要解决的技术问题采用以下技术方案来实现:一种阻燃的工艺品编织藤条处理方法,其特征在于:包括以下步骤,拣藤、打藤、洗藤、去皮、浸泡和干燥,所述的浸泡是采用药水浸泡,所述的药水按重量份包括以下组分,单质碘0.4~0.6份、聚乙烯吡咯烷酮0.8~1份、壬基酚聚氧乙烯醚0.4~0.6份、乙醇2~3份、纯净水80~120份和膨润土2~3份。所述的打藤是将藤条上的结疤去除。所述的浸泡液中还含有氯菌酸1~2份,三聚氰胺氰尿酸盐1~2份和氯化金钾3~4份。增加其阻燃性,不容易燃烧。所述的干燥时在遮阳的条件下通风干燥。避免下阳光直射,防止藤条干裂。所述的干燥后在藤条的表面附上一层耐火涂层,然后再风干。进一步增加其阻燃性能。所述打藤后的结疤处用聚酯蜡涂抹一层。表面光滑,防止结疤处进水霉变或生虫。所述的耐火涂层为为硼砂和氯化锌对水形成的混合物。阻燃性能好,表面强度高。本专利技术的有益效果是:本专利技术防止藤条受潮发霉,不容易生虫,阻燃效果好,强度高,增加编织品使用寿命。具体实施方式:为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实例,进一步阐述 ...
【技术保护点】
一种阻燃的工艺品编织藤条处理方法,其特征在于:包括以下步骤,拣藤、打藤、洗藤、去皮、浸泡和干燥,所述的浸泡是采用药水浸泡,所述的药水按重量份包括以下组分,氯菌酸1~2份,三聚氰胺氰尿酸盐1~2份和氯化金钾3~4份。
【技术特征摘要】
1.一种阻燃的工艺品编织藤条处理方法,其特征在于:包括以下步骤,拣藤、打藤、洗藤、去皮、浸泡和干燥,所述的浸泡是采用药水浸泡,所述的药水按重量份包括以下组分,氯菌酸1~2份,三聚氰胺氰尿酸盐1~2份和氯化金钾3~4份。2.根据权利要求1所述的一种阻燃的工艺品编织藤条处理方法,其特征在于:所述的打藤是将藤条上的结疤去除。3.根据权利要求1所述的一种阻燃的工艺品编织藤条处理方法,其特征在于:所述的浸泡液中还含有单质碘0.4~0.6份、聚乙烯吡咯烷酮0.8~1份、壬基酚聚氧乙烯醚0.4~0.6份、乙醇...
【专利技术属性】
技术研发人员:杨东志,
申请(专利权)人:安徽美景工艺品有限公司,
类型:发明
国别省市:安徽;34