The invention provides a low stress cracking of high strength inorganic insulation board, its components and components for quality copies were: 170 to 190 parts: cement, admixture: 30 - 40, 3 - 5, hydrogen peroxide: polypropylene fiber: 1 - 3, water: 85 ~ 95 and additive: 3 ~ 7, the invention adopts the formula and methods of innovation, in order to ensure the insulation board has excellent mechanical performance at the same time, also has the heat insulation, good waterproof performance, greatly improve the quality of products, and also can effectively avoid the cracking and water seepage, which is still in use later to ensure the excellent performance, and moderate cost, simple preparation method.
【技术实现步骤摘要】
本专利技术属于保温
,具体涉及一种低应力高强防裂无机保温板。
技术介绍
保温材料不仅能够起到对墙体、底面等主体结构的保护作用,同时能够有效降低外界温湿度以及各种因素对主体内部的影响。选择合适的保温材料不仅能达到保温节能的目的,还能提升主体结构的使用效果。保温材料主要分为有机保温材料与无机保温材料两种,有机保温材料具有良好的保温性能,但是其防火性能达不到标准要求,因此用作建筑室内保温板较少;无机保温材料虽然具有良好的防火性能,但是其保温性能却不能满足人们的需求;并且保温材料在长时间使用后,及其容易出现开裂、渗水等问题,严重影响了其使用安全稳定性以及保温效果。因此,研制出一种保温、防火效果好,且经久耐用的无机保温板是本领域技术人员所急需解决的难题。
技术实现思路
为解决上述问题,本专利技术公开了一种低应力高强防裂保温板。为了达到上述目的,本专利技术提供如下技术方案:一种低应力高强防裂无机保温板,其组成成分以及各成分所占质量份数分别为:水泥:170~190份、掺和料:30~40份、双氧水:3~5份、聚丙烯纤维:1~3份、水:85~95份、外加剂:3~7份。进一步地,其制备方法包括:(1)按照2:1质量比取用水泥与水,放入搅拌罐中搅拌均匀,加入掺和料、双氧水、聚丙烯纤维以及外加剂后再次搅拌均匀,初凝1~2h;(2)初凝完成后静置10h,进行脱模;(3)脱模后自然养护3~5天,成型为坯料;(4)根据需要对坯料进行切割,获得成品。本专利技术提供了一种低应力抗裂保温板,由水泥、掺合料、双氧水、聚丙烯纤维、水以及外加剂组成,水泥作为材料,加入掺合料能够进行一定的改性、 ...
【技术保护点】
一种低应力高强防裂无机保温板,其特征在于:其组成成分以及各成分所占质量份数分别为:水泥:170~190份、掺和料:30~40份、双氧水:3~5份、聚丙烯纤维:1~3份、水:85~95份、外加剂:3~7份。
【技术特征摘要】
1.一种低应力高强防裂无机保温板,其特征在于:其组成成分以及各成分所占质量份数分别为:水泥:170~190份、掺和料:30~40份、双氧水:3~5份、聚丙烯纤维:1~3份、水:85~95份、外加剂:3~7份。2.根据权利要求1所述的一种低应力高强防裂无机保温板,其特征在于:其制备方法包括:(1)按照2:1质量比取用水泥与水,放入搅拌罐中搅拌均匀,加入掺和料、双氧水、聚丙烯纤维以及外加剂后再次搅拌均匀,初凝1~2h;(2)初凝完成后静置10h,进行脱模;(3)脱模后自然养护3~5天,成型为坯料;(4)根据需要对坯料进行切割,获得成品。3.根据权利...
【专利技术属性】
技术研发人员:胡峻,周玉勤,花旺,蒋振军,胥明泽,周明华,
申请(专利权)人:江苏金贸科技发展有限公司,
类型:发明
国别省市:江苏;32