转印棉布褶皱雪纺面料制造技术

本发明专利技术涉及一种转印棉布褶皱雪纺面料。包括褶皱层（2）和内层（1）组成，褶皱层固定在内层上，褶皱层热压出褶皱形状，褶皱（2‑1）是均匀分布的。所述内层背面设置有衬里织物层，所述衬里织物层，为一种织物转移膜，包括双向拉伸聚酯BOPET薄膜，在所述BOPET薄膜表面上依次设置离型层、着色层、镀铝层和底胶层。本发明专利技术既满足穿着的舒适性又能提高褶皱层的美感。本发明专利技术转印。

Transfer cotton fabric

The invention relates to a transfer cotton cloth folding Chiffon fabric. Including the fold layer (2) and the inner layer (1), the fold layer is fixed on the inner layer, layer of hot extruded shape fold fold, fold (2 1) is evenly distributed. The inner lining layer are arranged on the back of the fabric, the fabric lining layer, a fabric transfer film, including biaxially oriented polyester film BOPET, on the surface of BOPET film are sequentially arranged on a release layer, a color layer, aluminized layer and bottom layer. The invention not only satisfies the wearing comfort, but also improves the aesthetic feeling of the fold layer. Transfer printing.

【技术实现步骤摘要】

本专利技术涉及一种面料，尤其涉及一种制作雪纺服装，属于纺织面料领域。
技术介绍
雪纺面料质地柔软、轻薄透明，手感滑爽富有弹性，外观清淡爽洁，具有良好的透气性和悬垂性。在女性服装里，雪纺面料使用的比较频繁，有雪纺衬衫、雪纺连衣裙、雪纺套裙，但纯雪纺布料制成的服装牢固性和易打理性不好。很难在外表面加工褶皱，外表没有立体感，满足不了人们多方位的需求。
技术实现思路
本专利技术的目的在于克服上述不足，提供一种由两层材料形成的棉布褶皱雪纺面料，该褶皱雪纺面料的外形美观时尚，制作简单，保持面料原有的颜色，内部雪纺材质垂坠，触感舒适。本专利技术的目的是这样实现的：一种转印棉布褶皱雪纺面料，包括褶皱层和内层组成，所述褶皱层通过缝合固定在内层上，所述褶皱层采用棉布制作，并热压出褶皱形状，所述褶皱是均匀分布的，所述褶皱之间的间距为3mm，所述内层由雪纺制成。所述内层背面设置有衬里织物层，所述衬里织物层，为一种织物转移膜，包括双向拉伸聚酯BOPET薄膜，在所述BOPET薄膜表面上依次设置离型层、着色层、镀铝层和底胶层。与现有技术相比，本专利技术的有益效果是：褶皱层采用棉布面料制作，并缝合在内层上，工艺简单，本文档来自技高网...

【技术保护点】
一种转印棉布褶皱雪纺面料，其特征在于：包括褶皱层（2）和内层（1）组成，所述褶皱层（2）通过缝合固定在内层（1）上，所述褶皱层（2）的褶皱（2‑1），是均匀分布的；所述褶皱(2‑1) 之间的间距为3mm；所述内层背面设置有衬里织物层，所述衬里织物层，为一种织物转移膜，包括双向拉伸聚酯BOPET薄膜，在所述BOPET薄膜表面上依次设置离型层、着色层、镀铝层和底胶层。

【技术特征摘要】
1.一种转印棉布褶皱雪纺面料，其特征在于：包括褶皱层（2）和内层（1）组成，所述褶皱层（2）通过缝合固定在内层（1）上，所述褶皱层（2）的褶皱（2-1），是均匀分布的；所述褶皱(2-1...