The invention discloses a preparation method of flower-like micron silver powder with slender and long petals. The preparation method comprises the following steps: adding ascorbic acid solution to silver nitrate solution at a certain stirring rate, reacting at 20-30 C for 5-10 minutes, then washing silver powder with a large amount of deionized water immediately, and drying to obtain flower-like micron silver powder with long petals. This method does not need additional surfactants and other substances. The preparation process is simple and feasible. The obtained silver powder has uniform morphology, high purity and high conversion, which is suitable for practical production.
【技术实现步骤摘要】
一种具有细长大花瓣的花朵状微米银粉的制备方法
本专利技术属于金属粒子合成
,特别涉及具有细长大花瓣的花朵状微米银粉的制备方法。
技术介绍
银粉可广泛应用到导电橡胶、导电胶粘剂、导电涂料等方面,涉及电子设备、催化、抗菌、电磁屏蔽等众多领域。目前,应用较广的银粉主要是通过球磨法或化学合成法制备的片状、球状及类球状银粉,如中国专利一种小粒径片状银粉的制备方法(CN108405859A)、分散性好的超细银粉的制备方法(CN105345023A)等。此外,也有关于用化学合成法制备多边形银粉(CN1401452A)、棒状银粉(CN1059211765A)、树枝状银粉(CN101811196A、CN101353814A)的报道。近来,中国专利(CN106424752A、CN101579746A)公开了具有花朵状微观结构的银粉,应用于导电油墨中,可提升导电油墨的导电性。但专利CN106424752A中需要使用第一还原剂溶液、第二还原剂溶液、表面活性剂溶液,专利CN101579746A中需要向可溶性银盐和还原剂中添加酸或醇,因此制备过程都比较复杂。此外,制备的银粉的花朵状结构上花瓣都比较小。
技术实现思路
针对以上情况,本专利技术提供一种简单的制备具有细长大花瓣的花朵状微米银粉的方法。此方法不需要添加表面活性剂等物质、操作简单,并且制得的银粉纯度高、产量大,适合实际生产。本专利技术的技术方案如下:本专利技术提供的一种具有细长大花瓣的花朵状微米银粉的制备方法,其特征是:将硝酸银溶解于水中,得到硝酸银水溶液;将还原剂抗坏血酸溶解于水中,得到抗坏血酸的水溶液;将抗坏血酸水溶液迅 ...
【技术保护点】
1.一种具有细长大花瓣的花朵状微米银粉的制备方法,其特征是:将硝酸银溶解于水中,得到硝酸银水溶液;将还原剂抗坏血酸溶解于水中,得到抗坏血酸水溶液;将抗坏血酸水溶液迅速地加入到一定搅拌速率的硝酸银水溶液中,20~30℃反应5~10分钟,之后立即用大量去离子水洗涤银粉,干燥后得到具有细长大花瓣的花朵状微米银粉。
【技术特征摘要】
1.一种具有细长大花瓣的花朵状微米银粉的制备方法,其特征是:将硝酸银溶解于水中,得到硝酸银水溶液;将还原剂抗坏血酸溶解于水中,得到抗坏血酸水溶液;将抗坏血酸水溶液迅速地加入到一定搅拌速率的硝酸银水溶液中,20~30℃反应5~10分钟,之后立即用大量去离子水洗涤银粉,干燥后得到具有细长大花瓣的花朵状微米银粉。2.权利要求1所述的一种具有细长大花瓣的花朵状微米银粉的制备方法,其特征在于所述硝酸银水溶...