The invention discloses a preparation method of nano-gold, which is characterized by the following preparation steps: (1) material preparation: preparation of chloroauric acid solution with mass percentage concentration of 0.01%-0.06% and allocation of tartaric acid or tartrate solution with mass percentage concentration of 2.5%; (2) system reaction: heating the prepared chloroauric acid solution to 70 ~100 (?) In the stirring state, the tartaric acid or tartrate solution prepared by step 1 was added, so that the percentage concentration of tartaric acid or tartrate in the reaction system was 0.01%-0.1%, and the stirring speed was 100-250rpm/min. After the addition of tartaric acid or tartrate, nano-gold solution was obtained after 3-5 minutes. Compared with the prior art, the invention has the advantages of green environmental protection, simple process and low cost.
【技术实现步骤摘要】
一种纳米金的制备方法
本专利技术属于材料制备
,具体的说,本专利技术涉及利用酒石酸或就是酸盐作为还原剂和稳定剂合成纳米金的方法。
技术介绍
纳米金是指金的微小颗粒,通常在水溶液中以胶体金的形态存在。胶体金的性质主要取决于金颗粒的直径及其表面特性。纳米金是研究较早的一种纳米材料,近年来纳米金的研究迅速发展并越来越受到重视。纳米金因其具有独特的性能而得到广泛重视,其制备与应用已成为当今纳米
中的一个研究热点。纳米金及其复合物因其具有表面效应、量子尺寸效应、光学效应等性能使其在工业催化、生物医药、生物分析化学、食品安全快速检测、光学探针、传感器等众多方面有着广泛潜在的应用前景。纳米金除具有一般纳米粒子的特性外,还具有良好的生物相容性,在许多领域有着极其广泛的应用。纳米金作为纳米粒子中应用较为成熟的纳米探针,在当今的生物分析化学中具有重要作用。纳米金的制备始于20世纪80年代末,其制备方法总体上分为物理方法和化学方法。化学方法中,常见方法有白磷还原法、抗坏血酸还原法、柠檬酸钠还原法及鞣酸-柠檬酸钠还原法等。还原剂的选择与制备的纳米金颗粒的大小有关。一般来说,备 ...
【技术保护点】
1.一种纳米金的制备方法,其特征在于:包含如下制备步骤:①、材料准备:制备质量百分比浓度为0.01%~0.06%%的氯金酸溶液和配置质量百分比浓度为2.5%的酒石酸或酒石酸盐溶液;②、体系反应:将步骤①准备的氯金酸溶液加热至温度为70℃~100℃时,搅拌状态下加入步骤①准备的酒石酸或酒石酸盐溶液,使加入的酒石酸或酒石酸盐占反应体系的质量百分比浓度为0.01%~0.1%,搅拌转速为100~250rpm/min,酒石酸或酒石酸盐加入结束后,维持3~5min后,即得到纳米金溶液。
【技术特征摘要】
1.一种纳米金的制备方法,其特征在于:包含如下制备步骤:①、材料准备:制备质量百分比浓度为0.01%~0.06%%的氯金酸溶液和配置质量百分比浓度为2.5%的酒石酸或酒石酸盐溶液;②、体系反应:将步骤①准备的氯金酸溶液加热至温度为70℃~100℃时,搅拌状态下加入步骤①准备的酒石酸或酒石酸盐溶液,使加入的酒石酸或酒石酸盐占反应体系的质量百分比浓度为0.01%~0.1%,搅拌转速为10...