The present invention relates to a wear-resisting and aging-resisting shock absorber rubber. The components of the wear-resisting and aging-resisting shock absorber rubber are as follows: chlorinated polyethylene rubber 20 25 phr, acrylonitrile-butadiene-styrene terpolymer 15 20 phr, BUTADIENE-NITRILE rubber 20 25 phr, polytetrafluoroethylene 5 10 phr, hexachlorodiphenol methane 15 phr phr phr, dihydroxymethylene urea 2 5 phr. 7 9 copies of high silica fiber, 2 4 copies of anti-aging agent and 1 3 copies of vulcanization accelerator. The invention has the advantages of simple manufacturing process, easy purchase of raw materials, low manufacturing cost, good wear resistance, good aging resistance and broad application prospects.
【技术实现步骤摘要】
一种耐磨耐老化减震橡胶
本专利技术涉及橡胶制品
,尤其涉及一种耐磨耐老化减震橡胶。
技术介绍
减震橡胶制品用于消除或减少机械震动的传递,达到减震、消音及减少冲击所致危害。其中包括橡胶减震器、橡胶缓冲器(块、垫)、橡胶连接件、空气弹簧及橡胶护弦等。众所周知,橡胶减震制品,易受温度、油质、日光及化学溶剂侵蚀,造成性能变化及老化,易松弛,使用寿命较短。
技术实现思路
为解决上述问题,本专利技术提供了一种耐磨耐老化减震橡胶。本专利技术的技术方案如下:一种耐磨耐老化减震橡胶,其特征在于:所述耐磨耐老化减震橡胶的组分按照重量份如下所示:氯化聚乙烯橡胶20-25份,丙烯腈-丁二烯-苯乙烯三元共聚物15-20份,丁腈橡胶20-25份,聚四氟乙烯5-10份,六氯二苯酚基甲烷15-20份,二羟甲基二羟基环乙烯脲2-5份,高硅氧纤维7-9份,抗老化剂2-4份,硫化促进剂1-3份。进一步的,所述抗老化剂为硫代双甲基苯酚、甲基丁苯基丁烷和硫代二丙酸双十八醇酯中的一种。进一步的,所述硫化促进剂为乙烯硫脲、二硫代氨基甲酸盐中的一种。更进一步的,一种耐磨耐老化减震橡胶制备方法,其特征在于:S1:按比例将氯化聚乙烯橡胶,丙烯腈-丁二烯-苯乙烯三元共聚物,丁腈橡胶,聚四氟乙烯,六氯二苯酚基甲烷,二羟甲基二羟基环乙烯脲,硫化促进剂放入反应釜内,于80-90℃条件下高速搅拌5h;S2:在反应釜中加入高硅氧纤维,低速搅拌1h后高速搅拌5h;S3:将反应釜冷却降温至40-60℃加入抗老化剂低速搅拌15h,冷却至室温,静置1h后即可得到成品。借由上述方案,本专利技术至少具有如下优点:本专利技术制作工 ...
【技术保护点】
1.一种耐磨耐老化减震橡胶,其特征在于:所述耐磨耐老化减震橡胶的组分按照重量份如下所示:氯化聚乙烯橡胶20‑25份,丙烯腈‑丁二烯‑苯乙烯三元共聚物15‑20份,丁腈橡胶20‑25份,聚四氟乙烯5‑10份,六氯二苯酚基甲烷15‑20份,二羟甲基二羟基环乙烯脲2‑5份,高硅氧纤维7‑9份,抗老化剂2‑4份,硫化促进剂1‑3份。
【技术特征摘要】
1.一种耐磨耐老化减震橡胶,其特征在于:所述耐磨耐老化减震橡胶的组分按照重量份如下所示:氯化聚乙烯橡胶20-25份,丙烯腈-丁二烯-苯乙烯三元共聚物15-20份,丁腈橡胶20-25份,聚四氟乙烯5-10份,六氯二苯酚基甲烷15-20份,二羟甲基二羟基环乙烯脲2-5份,高硅氧纤维7-9份,抗老化剂2-4份,硫化促进剂1-3份。2.根据权利要求1所述的一种耐磨耐老化减震橡胶,其特征在于:所述抗老化剂为硫代双甲基苯酚、甲基丁苯基丁烷和硫代二丙酸双十八醇酯中的一种。3.根据权利要求1所述的一种耐磨...
【专利技术属性】
技术研发人员:徐亚敏,
申请(专利权)人:丹阳西联生物技术有限公司,
类型:发明
国别省市:江苏,32