The invention discloses a preparation method of alloy magnesium bar, which comprises the following steps: adding copper, sodium and magnesium into industrial furnace for smelting; gradually adding magnesium ingot until the composition requirements are met, in which the mass percentage content of copper is 0.1 2%, the mass percentage content of sodium is 0.05 0.1%, and the rest is said magnesium; adding refining agent for stirring refining; and refining the alloy melt which will be finished by refining. The temperature is controlled at 450 500 C. The alloy magnesium rod is obtained by pressure extrusion. The alloy magnesium bars prepared by this method can be drawn into different lengths, diameters and shapes according to the requirements. The mechanical properties and corrosion resistance of the alloy magnesium bars are similar to those of brass bars, and the cost is greatly reduced.
【技术实现步骤摘要】
一种合金镁棒的制备方法
本专利技术涉及一种镁棒制备
,特别涉及一种铜钠镁合金镁棒。
技术介绍
黄铜棒被广泛的应用于空调管、冰箱管、机油管、给水管道以及各种机械配套用料,但是铜的价格居高不下,导致黄铜棒的成本很高。使用一种价格较低的金属棒材代替黄铜棒,已成为行业内共同面对的难题。
技术实现思路
本专利技术的目的是提供一种合金镁棒的制备方法,该制备方法得到的合金镁棒可以根据需求拉成不同长度、直径、形状,其机械性能、抗腐蚀性能与黄铜棒相当,成本得到大幅度下降。本专利技术提供一种合金镁棒的制备方法,包含以下步骤:S1、将铜、钠和镁加入工业炉进行熔炼;S2、逐步加入镁锭,直到达到成分要求,其中铜的质量百分含量为0.1-2%,钠的质量百分含量为0.05-0.1%,其余为所述镁;S3、加入精炼剂,进行搅拌精炼;S4、将精炼完成的合金熔液进行保温,温度控制在450-500℃;S5、通过挤压、刨皮、拉丝,得到合金镁棒。该制备方法得到的铜钠镁合金镁棒,使用时,机械性能、抗腐蚀性能与黄铜棒相当,但是成本得到大幅度下降。在一些实施方式中,还包括加入0.1-0.2%的稀土进行搅拌精炼。加入稀土后,最后得到的合金镁棒的抗腐蚀能力更优异。在一些实施方式中,得到的镁棒的直径为5-100mm。可以根据需要,拉成不同直径的合金镁棒。在一些实施方式中,得到的合金镁棒的长度为0.1-20m。可以根据需要,拉成不同长度的合金镁棒。在一些实施方式中,得到的镁棒为圆棒或方棒或六角棒。可以根据需要,拉成不同形状的合金镁棒。在一些实施方式中,精炼剂包括氯化钠、氯化钾、氯化铵。这些是优选的精炼剂,精炼效果 ...
【技术保护点】
1.一种合金镁棒的制备方法,其特征在于,包含以下步骤:S1、将铜、钠和镁加入工业炉进行熔炼;S2、逐步加入镁锭,直到达到成分要求,其中铜的质量百分含量为0.1‑2%,钠的质量百分含量为0.05‑0.1%,其余为所述镁;S3、加入精炼剂,进行搅拌精炼;S4、将精炼完成的合金熔液进行保温,温度控制在450‑500℃;S5、通过挤压、刨皮、拉丝,得到合金镁棒。
【技术特征摘要】
1.一种合金镁棒的制备方法,其特征在于,包含以下步骤:S1、将铜、钠和镁加入工业炉进行熔炼;S2、逐步加入镁锭,直到达到成分要求,其中铜的质量百分含量为0.1-2%,钠的质量百分...