The object of the present invention is to provide a method for synthesizing bismuth oxyiodate nanotablets by solid-phase chemical reaction. The method synthesizes bismuth oxyiodate nanotablets at room temperature by using cheap raw materials: solid bismuth nitrate and solid potassium iodate as reactants, using simple operation process, and through solid-phase and solid-phase direct chemical reaction. The method for preparing bismuth oxyiodate nanotablets provided by the invention has the characteristics of low cost, simple operation, short time and easy to realize mass production, which makes the invention have a very broad application prospect.
【技术实现步骤摘要】
一种固相化学反应合成碘酸氧铋纳米片的方法
本专利技术涉及一种固相化学反应合成碘酸氧铋纳米片的方法。
技术介绍
碘酸氧铋(BiOIO3)具有典型的Aurivillius层状结构,其结构由(Bi2O2)2+阳离子层和(IO3)-阴离子层相互交叉组成,是一种新的非中心对称和含有两个阳离子孤电子的极化材料。由于BiOIO3特殊的层状结构和内部的静电场有利于光生电子-空穴在BiO6和IO3多面锥上分离,因此其具有优异的光催化活性,2013年,张以和课题组首次将该材料用于光催化领域,BiOIO3纳米片的带隙为3.08eV,在紫外光下12min能完全降解甲基橙,远高于P25(TiO2)和其它含有(Bi2O2)2+层的铋基材料(BiOX(X=Cl,Br,I)和Bi2O2CO3)。2011年,Nguyen等人首次通过水热反应在200oC反应1周制备了BiOIO3材料。目前,BiOIO3纳米片的合成方法仍主要为水热法,虽然水热温度降低了40~50oC、时间缩短至5~10h,但该方法的高温高压环境仍然难以用于规模化生产。因此,选择一种简单易行的制备方法,制备碘酸氧铋纳米片具有十分重要的意义。固相化学合成法是两种或多种固体物质接触发生反应而得到相应产物的方法,具有工艺过程简单、产率高、不使用溶剂等优点,已经成为合成纳米材料的一种重要方法。
技术实现思路
本专利技术的目的在于提供一种固相化学反应合成碘酸氧铋纳米片的方法,该方法通过使用廉价的原料,采用简单的操作过程,经固相化学反应合成出碘酸氧铋纳米片。本专利技术用硝酸铋和碘酸钾作为反应物,在室温下通过固相化学反应合成前驱体,将前驱体在马 ...
【技术保护点】
1.一种固相化学反应合成碘酸氧铋纳米片的方法,其包括以下步骤 :将固体硝酸铋和固体碘酸钾混合,在室温条件下进行固相化学反应,反应产物经洗涤、干燥来制得前驱体,将前驱体在马弗炉中煅烧得到最终的碘酸氧铋纳米片。
【技术特征摘要】
1.一种固相化学反应合成碘酸氧铋纳米片的方法,其包括以下步骤:将固体硝酸铋和固体碘酸钾混合,在室温条件下进行固相化学反应,反应产物经洗涤、干燥来制得前驱体,将前驱体在马弗炉中煅烧得到最终的碘酸氧铋纳米片。2.按照权利要求1所述的一种固相化学反应合成碘酸氧铋纳米片的方法...