The invention provides a composite insulation foam cement board, cement board is composed of the following components quality copies of the components: 140 cement 160, fly ash 25 30 copies, 10 copies, 8 PP fiber calcium stearate 4 6 copies, 3 copies, 1 aluminum sulfate lignin sulfonate 0.5 0.8 0.4, triethanolamine 0.6, emulsion 2 4 copies, 1.6 copies, 1.2 foaming agent, foam stabilizing agent 0.4 0.6 copies, 1.2 copies, 0.8 hydrophober water 135 145. The invention also provides a preparation method thereof. Through the selection of the formula and the adjustment of the preparation method, the invention obtains a composite foaming cement board with high tensile and compressive strength and good heat insulation effect.
【技术实现步骤摘要】
一种保温复合发泡水泥板及其制备方法
本专利技术属于外墙外保温系统
,具体涉及一种保温复合发泡水泥板及其制备方法。
技术介绍
复合发泡板是一种经发泡、养护、切割等工艺制成的闭孔轻质无机发泡保温板,可用于房屋建筑的外墙外保温系统施工工程,替代原先普遍使用的聚苯板或挤塑板为代表的有机可燃性保温材料。现有复合发泡板抗拉强度、抗压强度太低。
技术实现思路
本专利技术提供了一种保温复合发泡水泥板,抗拉、抗压强度高,保温效果好。本专利技术提供一种保温复合发泡水泥板,所述水泥板由以下质量份数的各组分组成:水泥140-160份、粉煤灰25-30份、pp纤维8-10份、硬脂酸钙4-6份、硫酸铝1-3份、木质素磺酸盐0.5-0.8份、三乙醇胺0.4-0.6份、苯丙乳液2-4份、发泡剂1.2-1.6份、稳泡剂0.4-0.6份、憎水剂0.8-1.2份、水135-145份。作为优选,所述水泥板由以下质量份数的各组分组成:水泥150份、粉煤灰28份、pp纤维9份、硬脂酸钙5份、硫酸铝2份、木质素磺酸盐0.6份、三乙醇胺0.5份、苯丙乳液3份、发泡剂1.4份、稳泡剂0.5份、憎水剂1份、水140份。本专利技术还提供上述保温复合发泡水泥板的制备方法,在搅拌条件下,加入配方量的水泥、粉煤灰、硫酸铝、pp纤维和水,搅拌速率为600-800转/分,搅拌时间为100-130秒,然后加入配方量的其余组分,搅拌速率为1200-1400转/分,搅拌时间为90-110秒,注入模具,成型即得。本专利技术通过对配方的选择以及制备方法的调整,获得了一种抗拉、抗压强度高,保温效果好的复合发泡水泥板。具体实施方式 ...
【技术保护点】
一种保温复合发泡水泥板,其特征在于:所述水泥板由以下质量份数的各组分组成:水泥140‑160份、粉煤灰25‑30份、pp 纤维8‑10份、硬脂酸钙4‑6份、硫酸铝1‑3份、木质素磺酸盐0.5‑0.8份、三乙醇胺0.4‑0.6份、苯丙乳液2‑4份、发泡剂1.2‑1.6份、稳泡剂0.4‑0.6份、憎水剂0.8‑1.2份、水135‑145份。
【技术特征摘要】
1.一种保温复合发泡水泥板,其特征在于:所述水泥板由以下质量份数的各组分组成:水泥140-160份、粉煤灰25-30份、pp纤维8-10份、硬脂酸钙4-6份、硫酸铝1-3份、木质素磺酸盐0.5-0.8份、三乙醇胺0.4-0.6份、苯丙乳液2-4份、发泡剂1.2-1.6份、稳泡剂0.4-0.6份、憎水剂0.8-1.2份、水135-145份。2.根据权利要求1所述的保温复合发泡水泥板,其特征在于:所述水泥板由以下质量份数的各组分组成:水泥150份、粉煤灰...