The invention discloses a single wall corrugated pipe, which comprises the following ingredients with the ratio of PVC: 80 to 120 parts, calcium carbonate: 10 ~ 15, 3 ~ 6 compound stabilizer, stearic acid: 0.1 ~ 0.5, 0.2 ~ 0.7: polyethylene wax, chlorinated polyethylene: 5 - 15, titanium dioxide: 2 to 6 parts, processing aids: 1 ~ 5, 2 ~ 6: Anti granule. The invention has the advantages of good physical and mechanical properties such as resistance to granules, heat resistance, abrasion resistance, etc. the inner and the outer walls of the pipe are provided with regular and uniform size, and the product has no defects such as bubbles, cracks, cracks, depressions, impurities, etc..
【技术实现步骤摘要】
本专利技术涉及管材的
，特别是一种单壁波纹管的
技术介绍
塑料管材作为化学建材的重要组成部分，以其优越的性能，卫生、环保、低耗等为广大用户所广泛接受，主要有UPVC排水管，UPVC给水管，铝塑复合管，聚乙烯（PE）给水管材这几种。塑料管材是高科技复合而成的化学建材，而化学建材是继钢材、木材、水泥之后，当代新兴的第四大类新型建筑材料。化学建材在我国取得了长足进步迅猛发展，尤其是新型环保塑料管材的广泛使用，掀起了一声替代传统建材的革命。塑料管材因具有水流损失小、节能、节材、保护生态、竣工便捷等优点，广泛应用于建筑给排水、城镇给排水以及燃气管等领域，成为新世纪城建管网的主力军。
技术实现思路
本专利技术的目的就是解决现有技术中的问题，提出一种单壁波纹管，具有抗冲剂、耐热、耐磨等良好的物理力学性能，管道内外壁波纹规整，大小一致，产品不带有气泡、裂口、裂纹、凹陷、杂质等缺陷。为实现上述目的，本专利技术提出了一种单壁波纹管，包括以下组分且各组分的比例为聚氯乙烯：80～120份，碳酸钙：10～15份，复合稳定剂：3～6份，硬脂酸：0.1～0.5份，聚乙烯蜡：0.2～0.7份，氯化聚乙烯：5～15份，钛白粉：2～6份，加工助剂：1～5份，抗冲剂：2～6份。作为优选，所述碳酸钙采用轻质碳酸钙，所述复合稳定剂采用复合铅盐热稳定剂，所述复合铅盐热稳定剂由二盐基硬脂酸铅、三盐基硫酸铅和金属皂混合制得。作为优选，所述加工助剂采用丙烯酸酯类核壳共聚体，所述抗冲剂采用甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物。
【技术保护点】
一种单壁波纹管，其特征在于：包括以下组分且各组分的比例为聚氯乙烯：80～120份，碳酸钙：10～15份，复合稳定剂：3～6份，硬脂酸：0.1～0.5份，聚乙烯蜡：0.2～0.7份，氯化聚乙烯：5～15份，钛白粉：2～6份，加工助剂：1～5份，抗冲剂：2～6份。
【技术特征摘要】
1.一种单壁波纹管，其特征在于：包括以下组分且各组分的比例为聚氯乙烯：80～120份，碳酸钙：10～15份，复合稳定剂：3～6份，硬脂酸：0.1～0.5份，聚乙烯蜡：0.2～0.7份，氯化聚乙烯：5～15份，钛白粉：2～6份，加工助剂：1～5份，抗冲剂：2～6份。
2.如权利要求1所述的一种单壁波纹管，其特征在于：所述碳酸钙采用轻质碳酸钙，所述复合稳定剂采用复合铅盐热稳定剂，所述复合铅盐热稳定剂由二盐基硬脂酸铅、三盐基硫酸铅和金属皂混合制得。
3.如权利要求1所述的一种单壁波纹管，其特征在于：所述加工助剂采用丙烯酸酯类核壳共聚体，所述抗冲剂采用甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物。
4.如权利要求1所述的一种单壁波纹管，其特征在于：包括以下组分且...