The invention discloses a nanometer lanthanum nitrate and Zinc Oxide add in electrolyte technology to improve the performance of the alloy, micro arc oxidation equipment oxidation ceramic coating on the aluminum magnesium alloy surface, adding nano lanthanum nitrate and Zinc Oxide in the preparation of the electrolyte used in oxidation film, wherein when the concentration of lanthanum nitrate is 0.5g/L, nano Zinc Oxide was 3g/L. The present invention by adding lanthanum nitrate and nano Zinc Oxide micro arc oxidation of aluminum magnesium alloy in silicate system, micro arc oxidation ceramic coating after surface micro cracks and porosity decreased significantly, especially when the content of lanthanum nitrate is 0.5g/L, nano Zinc Oxide content is 3g/L, after microarc oxidation surface can obtain good comprehensive properties of ceramic film.
【技术实现步骤摘要】
本专利技术涉及一种在电解液中添加硝酸镧和纳米氧化锌提高合金性能的工艺,属于合金性能优化
技术介绍
随着机械零件轻量化的趋势使得高强韧铝合金有了更为广泛的应用。为了满足不断增大的需求,科研工作者对高强韧铸造铝合金进行了大量的科学研究,也取得了很多的成果。但怎么进一步提高已有的铸造铝合金的性能和开发研制新型的合金系列以满足各种需要,仍然是一个重要的课题。铝的电位一定程度上取决于陶瓷膜层的绝缘性能,改善其表面氧化陶瓷膜层的致密性能、增加膜层的厚度都有助于抗腐蚀性能的提高。一般来讲铝合金的腐蚀速度要比纯铝的快得多。微弧氧化技术在众多表面处理技术中突出出来,从引进研究到现在,虽然有许多成果和结论,但还处于研究阶段,未大规模投入工业生产。
技术实现思路
本专利技术要解决的问题:提供一种在电解液中添加硝酸镧和纳米氧化锌提高合金性能的工艺,旨在提高铝镁合金的性能,以满足工业的需求。本专利技术的技术方案:在电解液中添加硝酸镧和纳米氧化锌提高合金性能的工艺,采用微弧氧化设备在铝镁合金表面制备氧化陶瓷膜层,在制备氧化陶瓷膜层所用的电解液中添加硝酸镧和纳米氧化锌,所述当硝酸镧含量为0.5g/L,纳米氧化锌含量为3g/L。作为优选,所述的微弧氧化设备为双脉冲交流微弧氧化设备。作为优选,所述的电解液为硅酸盐电解液。本专利技术的有益效果:在硅酸盐体系中加入硝酸镧和纳米氧化锌对铝镁合金进行微弧氧化,微弧氧化后陶瓷膜层的表面微裂纹和孔隙率明显降低,尤其是当硝酸镧含量为0.5g/L,纳米氧化锌含量 ...
【技术保护点】
在电解液中添加硝酸镧和纳米氧化锌提高合金性能的工艺,其特征在于:采用微弧氧化设备在铝镁合金表面制备氧化陶瓷膜层,在制备氧化陶瓷膜层所用的电解液中添加硝酸镧和纳米氧化锌,所述当硝酸镧含量为0.5 g/L,纳米氧化锌含量为3 g/L。
【技术特征摘要】
1.在电解液中添加硝酸镧和纳米氧化锌提高合金性能的工艺,其特征在于:采用微弧氧化设备在铝镁合金表面制备氧化陶瓷膜层,在制备氧化陶瓷膜层所用的电解液中添加硝酸镧和纳米氧化锌,所述当硝酸镧含量为0.5g/L,纳米氧化锌含量为3g/L。
2.根据权利要求1...