一种单一试剂自反应制备二氧化钛纳米线的方法技术

本发明专利技术公开了一种单一试剂自反应制备二氧化钛纳米线的方法，含以下步骤：(1)取三氯化钛溶液作为起始原料，将三氯化钛溶液放入水热反应釜中，然后放入恒温箱中，调节反应温度为90～230℃，反应时间为1～100小时，反应后冷却至室温；(2)取出反应釜中的样品，清洗、烘干后获得二氧化钛纳米线。该方法工艺简单、易于操作控制、成本低、安全环保。

Method for preparing titania nanowire by self reaction of single reagent

The invention discloses a method for preparing a single reagent from the reaction of TiO2 nanowires, including the following steps: (1) the titanium trichloride solution as the starting material, the titanium trichloride solution into a hydrothermal reaction kettle, and then into the oven, adjusting the reaction temperature is 90 to 230 DEG C, the reaction time is 1 ~ 100 hours after the reaction, cooling to room temperature; (2) remove the reactor samples, washing and drying to obtain the titanium dioxide nano wire. The method has the advantages of simple process, easy operation and control, low cost, safety and environmental protection.

【技术实现步骤摘要】

[0001 ] 本专利技术具体涉及。
技术介绍
作为宽带隙(3.1eV)的η型半导体材料，二氧化钛已经在锂电池、光催化、染料敏化太阳电池等领域得到了深入研究和广泛应用。二氧化钛一维纳米结构如纳米线、纳米管和纳米片等由于其特殊的光、电、磁、化学和机械特性等而吸引了极大的关注。例如纳米线在上述应用中，可以提供一维的电子传输的通道，从而快速传输电子和减小电子-空穴的复合损失。已报道的合成二氧化钛纳米线的方法有电子束蒸发[Yang T S，etal.Surf Sci, 2004, 548:75],表面活性剂辅助合成法[Adachi M, et al., J Am ChemSoc, 2004，126:14943]，电喷涂法[Song M Y, et al., Appl Phys Lett, 2005，87:113113],电沉积法[Natarajan C，et al.J Electrochem Soc, 1996, 143:1547],强喊水热法[Enache-Pommer E, et al.，Appl.Phys.Lett.2007，91:123116.]和盐酸水热法[Liu B.e本文档来自技高网...

【技术保护点】
一种单一试剂自反应制备二氧化钛纳米线的方法，其特征是含以下步骤：(1)取三氯化钛溶液作为起始原料，将三氯化钛溶液放入水热反应釜中，然后放入恒温箱中，调节反应温度为90～230℃，反应时间为1～100小时，反应后冷却至室温；(2)取出反应釜中的样品，清洗、烘干后获得二氧化钛纳米线。

【技术特征摘要】
1.一种单一试剂自反应制备二氧化钛纳米线的方法，其特征是含以下步骤: (1)取三氯化钛溶液作为起始原料，将三氯化钛溶液放入水热反应釜中，然后放入恒温箱中，调节反应温度为90~230°C，反应时间为I~100小时，反应后冷却至室温； (2)取出反应釜中的样品，清洗、烘干后获得二氧化钛纳米线。2.根据权利要求1所述的单一试剂自反应制备二氧化钛纳米线的方法，其特征是:步骤(I)中三氯化钛溶液的质量百分含量为8%~30%，三氯化钛溶液体积占反应釜总体积的5% ~80%ο3.根据权利要求1所述的单一试剂自反应制备二氧化钛纳米线的方法，其...

【专利技术属性】
技术研发人员：刘勇，王晓悦，辛凌，李宝军，沈辉，
申请(专利权)人：中山大学，
类型：发明