一种棒状纳米羟基磷灰石的快速制备方法技术

本发明专利技术公开了一种棒状纳米羟基磷灰石的快速制备方法。该方法包括：1）十二烷基三甲基溴化铵和磷酸氢二钠反应；2）在步骤1）得到的混合溶液中滴加钙盐溶液进行反应；3）在120℃下继续反应；4）后处理。本发明专利技术所述棒状纳米羟基磷灰石的制备方法中采用十二烷基三甲基溴化铵作为调控剂，制备方法简单、条件温和可控，能够获得尺寸、形貌均匀可控的棒状纳米羟基磷灰石。此外十二烷基三甲基溴化铵具有良好的生物相容性，细胞实验证实本发明专利技术提供的棒状纳米羟基磷灰石可用于基因和药物载体的应用研究。

Rapid preparation method of rod-shaped nano hydroxyapatite

The invention discloses a rapid preparation method of rod-shaped nano hydroxyapatite. The method includes: 1) twelve alkyl three methyl bromide and two sodium hydrogen phosphate reaction; 2) in step 1) mixed solution obtained by dropping the calcium salt solution reaction; 3) to continue the reaction at 120 DEG C; 4) postprocessing. The rod like nano hydroxyapatite preparation method adopts twelve alkyl three methyl bromide as control agent, the preparation method is simple, mild and controllable conditions, can obtain the size and shape of rod like nano hydroxyapatite uniformly controllable. In addition, the twelve alkyl three ammonium bromide has good biocompatibility, and the cell proved that the rod-shaped nano hydroxyapatite provided by the invention can be applied to the study of gene and drug carriers.

【技术实现步骤摘要】

【技术保护点】
一种棒状纳米羟基磷灰石的快速制备方法，其特征在于包括以下工艺步骤：a)在30～70℃的反应温度下，将十二烷基三甲基溴化铵溶液加入到磷酸氢二钠溶液中，以200～500?rpm的速率搅拌均匀，使十二烷基三甲基溴化铵的终浓度为1.0×10?3～3.0×10?3?mol/L，用碱液调节混合溶液的pH值在11；b)在上述混合溶液中滴加钙盐溶液，得到棒状纳米羟基磷灰石溶液体系，最终反应体系中Ca/P摩尔比为1.67，滴加过程中，同时滴加碱性溶液，使反应体系的pH值维持在10～12，反应温度维持在60～70℃，搅拌速率维持在200～500?rpm；c)让该体系继续搅拌8～12小时后，将反应溶液置于120℃高压蒸汽环境中，待温度平衡后，静态反应1～2小时；d)反应完成后，8000～15000?rpm离心5～10分钟，分离沉淀，将沉淀先用去离子水超声清洗3次后分别离心处理，再用无水乙醇清洗3遍以上，将获得的样品在?50℃冷冻干燥或70?90℃快速鼓风干燥，得到棒状纳米羟基磷灰石。

【技术特征摘要】

【专利技术属性】
技术研发人员：孔祥东，赵瑞波，杨新燕，张祺，任小元，谢纯刚，
申请(专利权)人：浙江理工大学，
类型：发明
国别省市：