一种固体缓释型稳定性二氧化氯制造方法技术

一种固体缓释型稳定性二氧化氯制造方法，是将硫铝酸盐水泥熟料，无水硫酸钙，氧化钙和稳定性二氧化氯溶液混合调匀后倒入模具适中，凝固后即成含３２个结晶水的钙矾石体。使用时将固定酸化剂直接倒在其上即可产生二氧化氯气体，可用于空气消毒、灭菌、除臭。本发明专利技术制成的产品吸水率高，不易失水，成型性好，便于包装、运输，使用时不污染环境。特别适合冰箱、冷库、储藏室等处的空气净化，防止串味。（*该技术在2017年保护过期，可自由使用*）

Method for manufacturing solid slow-release type stable chlorine dioxide

A method for producing solid slow-release stable chlorine dioxide, the sulphoaluminate cement clinker, anhydrous calcium sulfate, calcium oxide and stability of chlorine dioxide solution mixture and mix thoroughly into the mold after moderate, solidification is ettringite body with 32 crystal water. When the utility model is used, the fixed acidifying agent can be directly poured on the chlorine dioxide gas, and the utility model can be used for air disinfection, sterilization and deodorization. The product of the invention has the advantages of high water absorption rate, water loss, good formability, convenient package and transportation and no pollution to environment. The utility model is especially suitable for the air purification of the refrigerator, the cold storage, the storage room, etc..

【技术实现步骤摘要】
本专利技术属于化工
，是一种制造固体二氧化氯的方法。二氧化氯是一种被世界卫生组织所确认的安全、高效、广谱无毒副作用的杀菌剂。它对环境、用品、食品的消毒、除臭、保鲜等方面有良好的作用。目前，生产固体稳定性二氧化氯的方法有多种，例如用沸石、硅酸盐等吸附稳定性二氧化氯溶液后得固体粉未，使用时与酸反应放出二氧化氯。见《沈阳化工》1994年第3期24页任孝林介绍的《固体状二氧化氯复合物》文章。这种粉未状产品，制造工艺复杂，包装和运输需要较高的条件，使用时易污染环境，另外仅靠物理吸附，所能吸附的二氧化氯液体量较少，而且易失水。本专利技术的目的是要提供一种能形成任意形状，且工艺简单，不易污染环境，可容纳大量二氧化氯液体的制造固体二氧化氯方法。本专利技术的解决方法是将硫铝酸盐水泥熟料，无水硫酸钙，氧化钙和稳定性二氧化氯溶液混合调匀后倒入模具中，凝固后即成一含32个结晶水的钙矾石体。其中各组成份的重量百分比为硫铝酸盐水泥熟料 16.7-25％。无水硫酸钙11.6-15％。氧化钙5-10％。稳定性二氧化氯溶液66.7-50％。使用时将固体酸化剂直接倒在含二氧化氯的钙矾石体上即可产生二氧化氯气体。固本文档来自技高网...

【技术保护点】
一种固体缓释型稳定性二氧化氯制造方法，是将硫酸盐水泥熟料，无水硫酸钙，氧化钙和稳定性二氧化氯溶液混合调匀后倒入模具中，凝固成形，其中各成份的重量百分比为：硫铝酸盐水泥熟料：１６．７－２５％。无水硫酸钙：１１．６－１５％。氧化钙： ５－１０％。稳定性二氧化氯溶液：６６．７－５０％。

【技术特征摘要】
1.一种固体缓释型稳定性二氧化氯制造方法，是将硫酸盐水泥熟料，无水硫酸钙，氧化钙和稳定性二氧化氯溶液混合调匀后倒入模具中，凝固成形，其中各...

【专利技术属性】
技术研发人员：赵恒，苏欣，李慧斌，
申请(专利权)人：东北煤炭工业环境保护研究所，
类型：发明
国别省市：22[中国|吉林]